EN 10222-5 Grade X2CrNiCu19-10 solution annealed (+AT)
EN 10222-5 Grade X2CrNiCu19-10 solution annealed (+AT) introduction
The corrosion resistant material X2CrNiCu19-10, material number 1.4650 is predominantly used for pressure vessel construction.
Equivalent material: DIN 1.4650, AISI 304LCu, SAE 304LCu, JIS SUS304L, EN 1.4650
EN 10222-5 Grade X2CrNiCu19-10 solution annealed (+AT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.9 g/cm³ |
EN 10222-5 Grade X2CrNiCu19-10 solution annealed (+AT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
EN 10222-5 Grade X2CrNiCu19-10 solution annealed (+AT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.03 % |
| Chromium |
Chromium of 18.5 - 20 % |
| Copper |
Copper of 1 % |
| Manganese |
Manganese of 2 % |
| Nickel |
Nickel of 9 - 10 % |
| Nitrogen |
Nitrogen of 0.08 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.015 % |
EN 10222-5 Grade X2CrNiCu19-10 solution annealed (+AT) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
EN 10222-5 Grade X2CrNiCu19-10 solution annealed (+AT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation |
20.0 °C |
Elongation of 40 - 45 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 520 - 720 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 210 MPa |
- |
| Yield strength Rp1.0 |
20.0 °C |
Yield strength Rp1.0 of 245 MPa |
- |
Partner with us to build a solid foundation for success, backed by our expertise in supplying high-quality steel materials.
-- Our promise