EN 10210-1 Grade S355NH hot finished
EN 10210-1 Grade S355NH hot finished introduction
Hot finished weldable structural hollow sections with circular, square, rectangular or elliptical cross-section for the steel and plant construction, civil engineering and vehicle construction.
Equivalent material: AS C350, ISO S355NH, ASTM A500 Grade C, UNS K02705, DIN StE355N, DIN 1.0539, DIN StE 355N, DIN S355NH, AFNOR S355NH, BS S355NH, EN 1.0539, UNS K02305, UNS K2803, UNS K12709, UNS K12437
EN 10210-1 Grade S355NH hot finished general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10210-1 Grade S355NH hot finished thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
EN 10210-1 Grade S355NH hot finished chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.02 % |
| Carbon |
Carbon of 0.2 % |
| Chromium |
Chromium of 0.3 % |
| Copper |
Copper of 0.35 % |
| Manganese |
Manganese of 0.9 - 1.65 % |
| Molybdenum |
Molybdenum of 0.1 % |
| Nickel |
Nickel of 0.5 % |
| Niobium |
Niobium of 0.05 % |
| Nitrogen |
Nitrogen of 0.02 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.5 % |
| Sulfur |
Sulfur of 0.03 % |
| Titanium |
Titanium of 0.03 % |
| Vanadium |
Vanadium of 0.12 % |
EN 10210-1 Grade S355NH hot finished magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10210-1 Grade S355NH hot finished electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
EN 10210-1 Grade S355NH hot finished mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation |
20.0 °C |
Elongation of 22 % |
- |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 20 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 470 - 630 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 335 - 355 MPa |
- |