EN 10132-3 Grade C22E soft annealed or soft annealed and skin passed (+A or +A+LC)
EN 10132-3 Grade C22E soft annealed or soft annealed and skin passed (+A or +A+LC) introduction
Cold-rolled narrow strip made of the mild steel C22E will be delivered in thicknesses up to 6 mm for quenching and tempering in following conditions:
- soft annealed or soft annealed and little rerolled (+A or +LC),
- cold rolled (+CR).
The delivery condition annealed to globular carbides (+AC) can be agreed.
Equivalent material: GB 20, GB U20202, ASTM A794 Grade 1023, UNS G10230, DIN Ck22, DIN 1.1151, DIN C22E, AFNOR C22E, AFNOR XC18, AFNOR XC25, BS C22E, BS En3A, BS En3C, BS 22CS, BS 22HS, BS 070M20, BS 055M15, BS En2, BS CS22, AISI 1023, AISI 1020, SAE 1023, SAE 1020, JIS S20C, JIS S20CK, EN 1.1151, ISO S20C, ISO CE20E4, ISO C22E, GOST 20, GB/T 20G, GB/T U50207, GB/T 20Z-III, GB/T 20, GB/T U20202, GB/T U50204, ASTM Grade 1020, UNS G10200
EN 10132-3 Grade C22E soft annealed or soft annealed and skin passed (+A or +A+LC) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
EN 10132-3 Grade C22E soft annealed or soft annealed and skin passed (+A or +A+LC) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.25E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.41E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 56.9 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 56.4 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 53.5 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 49.4 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 45.2 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 41.3 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 37.6 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 15.7 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 14.5 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 12.9 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 11.2 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 9.6 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.9 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 6.3 mm²/s |
- |
EN 10132-3 Grade C22E soft annealed or soft annealed and skin passed (+A or +A+LC) chemical
| Property |
Value |
| Carbon |
Carbon of 0.17 - 0.24 % |
| Chromium |
Chromium of 0.4 % |
| Manganese |
Manganese of 0.4 - 0.7 % |
| Molybdenum |
Molybdenum of 0.1 % |
| Nickel |
Nickel of 0.4 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.035 % |
EN 10132-3 Grade C22E soft annealed or soft annealed and skin passed (+A or +A+LC) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10132-3 Grade C22E soft annealed or soft annealed and skin passed (+A or +A+LC) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.83E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.27E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 2.95E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 3.8E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 4.81E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 5.99E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 7.38E-7 Ω·m |
EN 10132-3 Grade C22E soft annealed or soft annealed and skin passed (+A or +A+LC) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Elongation A80 |
20.0 °C |
Elongation A80 of 22 % |
- |
| Hardness, Rockwell B |
20.0 °C |
Hardness, Rockwell B of 78 [-] |
- |
| Hardness, Vickers |
20.0 °C |
Hardness, Vickers of 155 [-] |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.28 [-] |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 500 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 400 MPa |
- |
Withstand challenging environments and harsh conditions with our durable steel materials.
-- Our promise
Similar or equivalent steel materials