EN 10089 Grade 56Si7 quenched and tempered (+QT)
EN 10089 Grade 56Si7 quenched and tempered (+QT) introduction
The steel 56Si7 is used for hot formed springs, leaf springs up to 7 mm thickness, coil springs, spring plates and diaphragm springs for mechanical engineering.
Equivalent material: AS XK9258S, IS 55Si7, GOST 55S2, GOST 55С2, GOST 55S2A, GOST 55С2A, AISI 9255, UNS G92550, DIN 55Si7, DIN 1.5026, AFNOR 55S7, BS EN45, BS EN45 A, BS 250A53, BS 250A58, BS 250A61, AISI 9555, SAE 9555, EN 1.5026, GB 55Si2Mn
EN 10089 Grade 56Si7 quenched and tempered (+QT) general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
Typical for Steel |
EN 10089 Grade 56Si7 quenched and tempered (+QT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.52 - 0.6 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 1.6 - 2 % |
| Sulfur |
Sulfur of 0.025 % |
EN 10089 Grade 56Si7 quenched and tempered (+QT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 190 - 210 GPa |
Typical for Steel |
| Elongation |
20.0 °C |
Elongation of 6 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Reduction of area |
20.0 °C |
Reduction of area of 25 % |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 1450 - 1750 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 1300 MPa |
- |