EN 10088-1 Grade X2CrNi18-9 strain-hardened (+C700)
EN 10088-1 Grade X2CrNi18-9 strain-hardened (+C700) introduction
The austenitic steel X2CrNi18-9 is available in solution annealed condition in the form of cold rolled strip, warm rolled strip and warm rolled sheet. The material is resistant to intercrystalline corrosion also in welded condition.
Equivalent material: AISI 304L, ISO X2CrNi18-9, UNS S30403, AMS S30403, AMS 304L, ASME 304L, ASTM 304L, ASTM TP304L, ASTM WP304L, ASTM MT304L, ASTM P304L, ASTM F304L, ASTM S30403, SAE 304L, GB 022Cr19Ni10, GB S30403, ISO 4307-304-03-I, ISO AP27B, JIS SUS304L, ASTM A276Type304L, ASTM A314Type304L, ASTM A484Type304L, ASTM A666Type304L, AISI Type304L, DIN 1.4307, DIN G-X2CrNiN18-9, AFNOR Z3CN19-09, BS 304S11, SS 2352, EN 1.4307, GOST 03Ch18N11, GB 00Cr19Ni10, IS X02Cr18Ni11
EN 10088-1 Grade X2CrNi18-9 strain-hardened (+C700) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.9 g/cm³ |
EN 10088-1 Grade X2CrNi18-9 strain-hardened (+C700) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.6E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.65E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.7E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.8E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.8E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 15 W/(m·K) |
- |
EN 10088-1 Grade X2CrNi18-9 strain-hardened (+C700) chemical
| Property |
Value |
| Carbon |
Carbon of 0.03 % |
| Chromium |
Chromium of 17.5 - 19.5 % |
| Manganese |
Manganese of 2 % |
| Nickel |
Nickel of 8 - 10.5 % |
| Nitrogen |
Nitrogen of 0.11 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.015 % |
EN 10088-1 Grade X2CrNi18-9 strain-hardened (+C700) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 7.3E-7 Ω·m |
EN 10088-1 Grade X2CrNi18-9 strain-hardened (+C700) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 194 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 186 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 179 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 172 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 165 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 20 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 700 - 900 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 350 MPa |
- |
Our skilled craftsmen ensure meticulous attention to detail for superior steel products.