EN 10084 Grade C16R quenched (+Q)
EN 10084 Grade C16R quenched (+Q) introduction
The case-hardening steel is mainly used for gear parts, but also in the mechanical engineering.
Equivalent material: EN 1.1208, ISO C16R, ASTM A568 Grade 1016, UNS G10160, SAE 1016, DIN 1.1208, DIN C16R, AFNOR C16R, BS C16R, AISI 1016, ISO C16M2, ASTM Grade 1016
EN 10084 Grade C16R quenched (+Q) general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10084 Grade C16R quenched (+Q) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
EN 10084 Grade C16R quenched (+Q) chemical
| Property |
Value |
| Carbon |
Carbon of 0.12 - 0.18 % |
| Chromium |
Chromium of 0.4 % |
| Copper |
Copper of 0.3 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Molybdenum |
Molybdenum of 0.1 % |
| Nickel |
Nickel of 0.4 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.4 % |
| Sulfur |
Sulfur of 0.02 - 0.04 % |
EN 10084 Grade C16R quenched (+Q) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10084 Grade C16R quenched (+Q) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
EN 10084 Grade C16R quenched (+Q) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 600 - 800 MPa |
- |