EN 10084 Grade C16E quenched (+Q)
EN 10084 Grade C16E quenched (+Q) introduction
The case-hardening steel is mainly used for gear parts, but also in the mechanical engineering.
Equivalent material: AS 1016, AS K1016, GB 15Al, GB U22152, EN 1.1148, IS 14Mn4, ISO C16E, ASTM A29 Grade 1016, ASTM A568 Grade 1016, ASTM A576 Grade 1016, ASTM A659 Grade 1016, UNS G10160, SAE 1016, DIN Ck15Al, DIN 1.1148, DIN C16E, AFNOR C16E, BS C16E, BS En32C, BS S14, BS 4S14, BS 080A15, BS 080M15, AISI 1016, ISO C16E4, GB/T 15AI, GB/T U22152, ASTM Grade 1016
EN 10084 Grade C16E quenched (+Q) general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10084 Grade C16E quenched (+Q) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
EN 10084 Grade C16E quenched (+Q) chemical
| Property |
Value |
| Carbon |
Carbon of 0.12 - 0.18 % |
| Chromium |
Chromium of 0.4 % |
| Copper |
Copper of 0.3 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Molybdenum |
Molybdenum of 0.1 % |
| Nickel |
Nickel of 0.4 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.4 % |
| Sulfur |
Sulfur of 0.035 % |
EN 10084 Grade C16E quenched (+Q) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10084 Grade C16E quenched (+Q) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
EN 10084 Grade C16E quenched (+Q) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 600 - 800 MPa |
- |
Our stringent quality control measures ensure consistent and reliable steel products.
-- Our promise
Similar or equivalent steel materials