EN 10084 Grade C15R quenched (+Q)
EN 10084 Grade C15R quenched (+Q) introduction
Steel C15R is suitable for parts of slightly higher core strength in vehicle manufacturing and machine engineering, which are predominantly wear loaded (e.g. levers, joints, gear wheels).
The steel has an enhanced workability due to its controlled S-content.
Equivalent material: EN 1.1140, ISO C15R, SAE AISI1015, ASTM A576 Grade 1015, UNS G10150, DIN Cm15, DIN 1.1140, DIN C15R, AFNOR C15R, AISI 1015, SAE 1015, ISO C15M2, ASTM M1015, ASTM Grade 1015
EN 10084 Grade C15R quenched (+Q) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
EN 10084 Grade C15R quenched (+Q) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.1E-5 - 1.25E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.18E-5 - 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.41E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 460 - 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 - 480 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 - 520 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 57.5 - 58.7 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 54.4 - 55.7 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 50.2 - 51.9 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 47.6 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 43.4 - 44 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 39.6 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 36 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 15.9 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 14.3 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 12.5 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 10.8 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 9.2 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.6 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 6.1 mm²/s |
- |
EN 10084 Grade C15R quenched (+Q) chemical
| Property |
Value |
| Carbon |
Carbon of 0.12 - 0.18 % |
| Chromium |
Chromium of 0.4 % |
| Copper |
Copper of 0.3 % |
| Manganese |
Manganese of 0.3 - 0.6 % |
| Molybdenum |
Molybdenum of 0.1 % |
| Nickel |
Nickel of 0.4 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.4 % |
| Sulfur |
Sulfur of 0.02 - 0.035 % |
EN 10084 Grade C15R quenched (+Q) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10084 Grade C15R quenched (+Q) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.1E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.3E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.04E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 3.94E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.01E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.25E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 7.7E-7 Ω·m |
EN 10084 Grade C15R quenched (+Q) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 210 - 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 205 - 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 193 - 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 185 - 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 175 - 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 600 - 800 MPa |
- |
Our customized steel solutions ensure the perfect fit for your specific project requirements.