EN 10277-4 Grade C15R cold drawn
EN 10277-4 Grade C15R cold drawn introduction
Steel C15R is suitable for parts in vehicle and machine engineering with a slightly higher core strength that are predominantly wear loaded (e.g. levers, joints, gear wheels). The steel shows an enhanced workability due to its controlled S-content. Lowest application temperature -25°C, most favorable application area 5 to 10 mm nominal size.
As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).
Equivalent material: NBN C16-3, ISO C15M2, DIN Cm15, ASTM A108 Grade 1015, SAE 1015, UNS G10150, DIN 1.1140, DIN C15R, AFNOR C15R, AISI 1015, EN 1.1140, ISO C15R, ASTM M1015, ASTM Grade 1015
EN 10277-4 Grade C15R cold drawn general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
EN 10277-4 Grade C15R cold drawn thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.1E-5 - 1.25E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.18E-5 - 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.41E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Max service temperature, long |
- |
Max service temperature, long of -25 - 0 °C |
- |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 460 - 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 - 480 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 - 520 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 57.5 - 58.7 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 54.4 - 55.7 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 50.2 - 51.9 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 47.6 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 43.4 - 44 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 39.6 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 36 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 15.9 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 14.3 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 12.5 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 10.8 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 9.2 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.6 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 6.1 mm²/s |
- |
EN 10277-4 Grade C15R cold drawn chemical
| Property |
Value |
| Carbon |
Carbon of 0.12 - 0.18 % |
| Manganese |
Manganese of 0.3 - 0.6 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.02 - 0.04 % |
EN 10277-4 Grade C15R cold drawn magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10277-4 Grade C15R cold drawn electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.1E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.3E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.04E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 3.94E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.01E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.25E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 7.7E-7 Ω·m |
EN 10277-4 Grade C15R cold drawn mechanical
| Property |
Temperature |
Value |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
| - |
20.0 °C |
Elastic modulus of 210 - 212 GPa |
| - |
100.0 °C |
Elastic modulus of 205 - 207 GPa |
| - |
200.0 °C |
Elastic modulus of 193 - 199 GPa |
| - |
300.0 °C |
Elastic modulus of 185 - 192 GPa |
| - |
400.0 °C |
Elastic modulus of 175 - 184 GPa |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
| Elongation |
20.0 °C |
Elongation of 7 - 12 % |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.28 [-] |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
| Tensile strength |
20.0 °C |
Tensile strength of 340 - 800 MPa |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 215 - 380 MPa |