EN 10084 Grade C15E quenched (+Q)
EN 10084 Grade C15E quenched (+Q) introduction
Steel C15E is suitable for parts of slightly higher core strength, increased wear strain as well as of higher dimension and complexer form than standard mark C15 in vehicle manufacturing and machine engineering (e.g. levers, joints, gear wheels).
Equivalent material: GB 15, GB U20152, EN 1.1141, IS 15C8, ISO C15E, JIS S15C, GOST 15, KS SM15C, KS SM15CK, SAE 1015, ASTM A576 Grade 1015, ASTM A576 Grade 1016, UNS G10150, DIN Ck15, DIN 1.1141, DIN C15E, AFNOR C15E, AFNOR XC18, AFNOR C18RR, AFNOR XC15, BS 080M15, BS C15E, BS En32C, BS 080A15, UNI C16, SS 1370, UNE C15K, AISI 1015, AISI 1017, SAE 1017, JIS S15CK, ISO C15E4, ISO S15C, GB/T 15, GB/T U20152, ASTM M1015, ASTM Grade 1015, UNS G10170
EN 10084 Grade C15E quenched (+Q) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
EN 10084 Grade C15E quenched (+Q) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.1E-5 - 1.25E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.18E-5 - 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.41E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 460 - 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 - 480 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 - 520 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 57.5 - 58.7 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 54.4 - 55.7 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 50.2 - 51.9 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 47.6 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 43.4 - 44 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 39.6 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 36 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 15.9 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 14.3 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 12.5 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 10.8 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 9.2 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.6 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 6.1 mm²/s |
- |
EN 10084 Grade C15E quenched (+Q) chemical
| Property |
Value |
| Carbon |
Carbon of 0.12 - 0.18 % |
| Chromium |
Chromium of 0.4 % |
| Copper |
Copper of 0.3 % |
| Manganese |
Manganese of 0.3 - 0.6 % |
| Molybdenum |
Molybdenum of 0.1 % |
| Nickel |
Nickel of 0.4 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.4 % |
| Sulfur |
Sulfur of 0.035 % |
EN 10084 Grade C15E quenched (+Q) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10084 Grade C15E quenched (+Q) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.1E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.3E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.04E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 3.94E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.01E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.25E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 7.7E-7 Ω·m |
EN 10084 Grade C15E quenched (+Q) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 210 - 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 205 - 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 193 - 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 185 - 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 175 - 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 600 - 800 MPa |
- |