EN 10084 Grade 28CrS4 quenched (+Q)

EN 10084 Grade 28CrS4 quenched (+Q)

EN 10084 Grade 28CrS4 quenched (+Q) introduction

Steel 28CrS4 is suitable for smaller parts of slightly higher load and enhanced workability in vehicle manufacturing, engine and machine engineering (e.g. transmission gears, driving shafts).

Equivalent material: EN 1.7036, ISO 28CrS4, ASTM A434 Grade 5130, ASTM A914 Grade 5130RH, SAE 5130, SAE 5130H, SAE 5130RH, DIN 1.7036, DIN 28CrS4, AFNOR 28CrS4, BS 28CrS4, AISI 5130H, AISI 5130, UNS H51300, UNS G51300

EN 10084 Grade 28CrS4 quenched (+Q) general

Property Temperature Value
Density 20.0 °C Density of 7.83 g/cm³

EN 10084 Grade 28CrS4 quenched (+Q) thermal

Property Temperature Value Comment
Coefficient of thermal expansion -100.0 °C Coefficient of thermal expansion of 1.05E-5 1/K -
- 20.0 °C Coefficient of thermal expansion of 1.15E-5 1/K -
- 100.0 °C Coefficient of thermal expansion of 1.21E-5 1/K -
- 200.0 °C Coefficient of thermal expansion of 1.27E-5 1/K -
- 300.0 °C Coefficient of thermal expansion of 1.32E-5 1/K -
- 400.0 °C Coefficient of thermal expansion of 1.36E-5 1/K -
- 500.0 °C Coefficient of thermal expansion of 1.4E-5 1/K -
- 600.0 °C Coefficient of thermal expansion of 1.44E-5 1/K -
Melting point - Melting point of 1382 - 1529 °C Typical for Chromium Steel
Specific heat capacity -100.0 °C Specific heat capacity of 423 J/(kg·K) -
- 20.0 °C Specific heat capacity of 461 J/(kg·K) -
- 100.0 °C Specific heat capacity of 479 J/(kg·K) -
- 200.0 °C Specific heat capacity of 499 J/(kg·K) -
- 300.0 °C Specific heat capacity of 517 J/(kg·K) -
- 400.0 °C Specific heat capacity of 536 J/(kg·K) -
- 500.0 °C Specific heat capacity of 558 J/(kg·K) -
- 600.0 °C Specific heat capacity of 587 J/(kg·K) -
Thermal conductivity 20.0 °C Thermal conductivity of 45.1 W/(m·K) -
- 100.0 °C Thermal conductivity of 45.1 W/(m·K) -
- 200.0 °C Thermal conductivity of 44.1 W/(m·K) -
- 300.0 °C Thermal conductivity of 41.9 W/(m·K) -
- 400.0 °C Thermal conductivity of 39.4 W/(m·K) -
- 500.0 °C Thermal conductivity of 36.9 W/(m·K) -
- 600.0 °C Thermal conductivity of 34.4 W/(m·K) -
Thermal diffusivity 20.0 °C Thermal diffusivity of 12.5 mm²/s -
- 100.0 °C Thermal diffusivity of 11.6 mm²/s -
- 200.0 °C Thermal diffusivity of 10.6 mm²/s -
- 300.0 °C Thermal diffusivity of 9.5 mm²/s -
- 400.0 °C Thermal diffusivity of 8.4 mm²/s -
- 500.0 °C Thermal diffusivity of 7.1 mm²/s -
- 600.0 °C Thermal diffusivity of 5.8 mm²/s -

EN 10084 Grade 28CrS4 quenched (+Q) chemical

Property Value
Carbon Carbon of 0.24 - 0.31 %
Chromium Chromium of 0.9 - 1.2 %
Copper Copper of 0.4 %
Manganese Manganese of 0.6 - 0.9 %
Phosphorus Phosphorus of 0.03 %
Silicon Silicon of 0.4 %
Sulfur Sulfur of 0.02 - 0.04 %

EN 10084 Grade 28CrS4 quenched (+Q) electrical

Property Temperature Value
Electrical resistivity 20.0 °C Electrical resistivity of 2.31E-7 Ω·m
- 100.0 °C Electrical resistivity of 2.84E-7 Ω·m
- 200.0 °C Electrical resistivity of 3.58E-7 Ω·m
- 300.0 °C Electrical resistivity of 4.48E-7 Ω·m
- 400.0 °C Electrical resistivity of 5.52E-7 Ω·m
- 500.0 °C Electrical resistivity of 6.71E-7 Ω·m
- 600.0 °C Electrical resistivity of 8.06E-7 Ω·m

EN 10084 Grade 28CrS4 quenched (+Q) mechanical

Property Temperature Value Comment
Elastic modulus -100.0 °C Elastic modulus of 217 GPa -
- 20.0 °C Elastic modulus of 212 GPa -
- 100.0 °C Elastic modulus of 207 GPa -
- 200.0 °C Elastic modulus of 199 GPa -
- 300.0 °C Elastic modulus of 192 GPa -
- 400.0 °C Elastic modulus of 184 GPa -
- 500.0 °C Elastic modulus of 175 GPa -
- 600.0 °C Elastic modulus of 164 GPa -
Poisson's ratio 23.0 °C Poisson's ratio of 0.29 [-] Typical for Chromium Steel
Tensile strength 20.0 °C Tensile strength of 700 - 900 MPa -