EN 10277-5 Grade 28CrS4 cold drawn or turned and quenched and tempered
EN 10277-5 Grade 28CrS4 cold drawn or turned and quenched and tempered introduction
Steel 28 CrS 4 is suitable for smaller parts of a little higher load and enhanced workability in vehicle manufacturing, engine and machine engineering ( e.g. transmission gears, drive shafts). Lowest application temp. -25 °C.
Equivalent material: DIN 1.7036, AFNOR 28CrS4, BS 28CrS4, AISI 5130H, AISI 5130, SAE 5130H, SAE 5130, EN 28CrS4, EN 1.7036, UNS H51300, UNS G51300
EN 10277-5 Grade 28CrS4 cold drawn or turned and quenched and tempered general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.83 g/cm³ |
EN 10277-5 Grade 28CrS4 cold drawn or turned and quenched and tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.05E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.15E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.21E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.27E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.4E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.44E-5 1/K |
- |
| Max service temperature, long |
- |
Max service temperature, long of -25 - 0 °C |
- |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 45.1 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 45.1 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 44.1 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 41.9 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 39.4 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 36.9 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 34.4 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 12.5 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 11.6 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 10.6 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 9.5 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.4 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.1 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 5.8 mm²/s |
- |
EN 10277-5 Grade 28CrS4 cold drawn or turned and quenched and tempered chemical
| Property |
Value |
| Carbon |
Carbon of 0.24 - 0.31 % |
| Chromium |
Chromium of 0.9 - 1.2 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.02 - 0.035 % |
EN 10277-5 Grade 28CrS4 cold drawn or turned and quenched and tempered electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 2.31E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.84E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.58E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.48E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.52E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.71E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 8.06E-7 Ω·m |
EN 10277-5 Grade 28CrS4 cold drawn or turned and quenched and tempered mechanical
| Property |
Temperature |
Value |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
| - |
20.0 °C |
Elastic modulus of 212 GPa |
| - |
100.0 °C |
Elastic modulus of 207 GPa |
| - |
200.0 °C |
Elastic modulus of 199 GPa |
| - |
300.0 °C |
Elastic modulus of 192 GPa |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
| Elongation |
20.0 °C |
Elongation of 12 - 15 % |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.28 [-] |
| Reduction of area |
20.0 °C |
Reduction of area of 40 - 50 % |
| Tensile strength |
20.0 °C |
Tensile strength of 650 - 1000 MPa |
| Yield strength |
20.0 °C |
Yield strength of 410 - 650 MPa |
Our diverse range of steel products caters to endless applications across industries.