EN 10084 Grade 17CrS3 quenched (+Q)
EN 10084 Grade 17CrS3 quenched (+Q) introduction
The case-hardening steel is mainly used for gear parts, but also in the mechanical engineering.
Equivalent material: EN 1.7014, IS 15Cr3(-S), ISO 17CrS3, DIN 1.7014
EN 10084 Grade 17CrS3 quenched (+Q) general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Chromium Steel |
EN 10084 Grade 17CrS3 quenched (+Q) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 9.4E-6 - 1.5E-5 1/K |
Typical for Chromium Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 - 494 J/(kg·K) |
Typical for Chromium Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 23 - 50 W/(m·K) |
Typical for Chromium Steel |
EN 10084 Grade 17CrS3 quenched (+Q) chemical
| Property |
Value |
| Carbon |
Carbon of 0.14 - 0.2 % |
| Chromium |
Chromium of 0.7 - 1 % |
| Copper |
Copper of 0.4 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.4 % |
| Sulfur |
Sulfur of 0.02 - 0.04 % |
EN 10084 Grade 17CrS3 quenched (+Q) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Chromium Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 600 - 800 MPa |
- |