EN 10028-5 Grade P460M thermomechanically rolled
EN 10028-5 Grade P460M thermomechanically rolled introduction
Fine grain weldable thermomechanically rolled structural steel for pressure vessel application
Application temperature: -20 to 20 °C
Equivalent material: ASTM A738 Grade A, UNS K12447, IS P460M, DIN StE460TM, DIN BStE460TM, DIN FStE460TM, DIN 1.8826, DIN FStE 460 TM, DIN P460M, EN 1.8826
EN 10028-5 Grade P460M thermomechanically rolled general
| Property |
Value |
Comment |
| Density |
Density of 7.8 g/cm³ |
Typical for Steel |
EN 10028-5 Grade P460M thermomechanically rolled thermal
| Property |
Value |
Comment |
| Coefficient of thermal expansion |
Coefficient of thermal expansion of 11.72 1/K |
Predicted Value |
| Specific heat capacity |
Specific heat capacity of 453.8 J/(kg·K) |
Predicted Value |
| Thermal conductivity |
Thermal conductivity of 37.79 W/(m·K) |
Predicted Value |
EN 10028-5 Grade P460M thermomechanically rolled chemical
| Property |
Value |
Condition |
Related Standards |
Shape |
| Aluminium |
Aluminium of 0.02 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| Carbon |
Carbon of 0.16 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| Manganese |
Manganese of 1.7 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| Molybdenum |
Molybdenum of 0.2 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| Nickel |
Nickel of 0.5 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| Niobium |
Niobium of 0.05 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| Nitrogen |
Nitrogen of 0.02 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| Phosphorus |
Phosphorus of 0.025 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| Silicon |
Silicon of 0.6 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| Sulfur |
Sulfur of 0.01 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| - |
Sulfur of 0.02 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| Titanium |
Titanium of 0.05 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| Vanadium |
Vanadium of 0.1 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
EN 10028-5 Grade P460M thermomechanically rolled electrical
| Property |
Value |
Comment |
| Electrical conductivity |
Electrical conductivity of 7 S/m |
Predicted Value |
| Electrical resistivity |
Electrical resistivity of 33 Ω·m |
Predicted Value |
EN 10028-5 Grade P460M thermomechanically rolled mechanical
| Property |
Temperature |
Value |
Condition |
Related Standards |
Shape |
Comment |
| Elastic modulus |
- |
Elastic modulus of 190 - 210 GPa |
- |
- |
- |
Typical for Steel |
| Elongation |
- |
Elongation of 13.4 % |
- |
- |
- |
Predicted Value, A200 |
| - |
- |
Elongation of 15.3 % |
- |
- |
- |
Predicted Value, A80 |
| - |
- |
Elongation of 17.6 % |
- |
- |
- |
Predicted Value, Transverse |
| - |
- |
Elongation of 19.0 % |
- |
- |
- |
Predicted Value, A80 Transverse |
| - |
- |
Elongation of 20.4 % |
- |
- |
- |
Predicted Value, A5 |
| - |
- |
Elongation of 22.2 % |
- |
- |
- |
Predicted Value, A50 |
| - |
20 °C |
Elongation of 17 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
- |
| Poisson's ratio |
- |
Poisson's ratio of 0.3 [-] |
- |
- |
- |
Typical for Steel |
| Reduction of area |
- |
Reduction of area of 39.6 % |
- |
- |
- |
Predicted Value |
| - |
- |
Reduction of area of 44.2 % |
- |
- |
- |
Predicted Value, Transverse |
| Shear modulus |
- |
Shear modulus of 80.0 GPa |
- |
- |
- |
Predicted Value |
| Shear strength |
- |
Shear strength of 558.2 MPa |
- |
- |
- |
Predicted Value |
| Tensile strength |
20 °C |
Tensile strength of 530 - 720 MPa |
thermomechanically rolled |
EN 10028-5 |
Flat |
- |
| Yield strength |
- |
Yield strength of 261.9 MPa |
- |
- |
- |
Predicted Value, RP1 |
| - |
- |
Yield strength of 318.9 MPa |
- |
- |
- |
Predicted Value, RP1 Transverse |
| - |
- |
Yield strength of 430.3 MPa |
- |
- |
- |
Predicted Value, RP02 |
| - |
- |
Yield strength of 438.9 MPa |
- |
- |
- |
Predicted Value, Transverse |
| - |
- |
Yield strength of 462.2 MPa |
- |
- |
- |
Predicted Value, RP02 Transverse |
| - |
- |
Yield strength of 524.6 MPa |
- |
- |
- |
Predicted Value, RP05 |
| - |
- |
Yield strength of 525.5 MPa |
- |
- |
- |
Predicted Value, RP002 |
| - |
20 °C |
Yield strength of 430 MPa |
thermomechanically rolled |
EN 10028-5 |
Flat |
- |
| - |
20 °C |
Yield strength of 440 MPa |
thermomechanically rolled |
EN 10028-5 |
Flat |
- |
| - |
20 °C |
Yield strength of 460 MPa |
thermomechanically rolled |