EN 10028-5 Grade P355ML1 thermomechanically rolled
EN 10028-5 Grade P355ML1 thermomechanically rolled introduction
The low-temperature tough fine grain structural steel is used for pressure vessels up to -40 °C.
The steel is suitable for welding processes in current use.
Equivalent material: ASTM A515 Grade 65, UNS K02800, IS P355ML1, DIN TStE355TM, DIN BTStE355TM, DIN 1.8832, DIN FTStE 315 TM, DIN P355ML1, EN 1.8832
EN 10028-5 Grade P355ML1 thermomechanically rolled general
| Property |
Value |
Comment |
| Density |
Density of 7.8 g/cm³ |
Typical for Steel |
EN 10028-5 Grade P355ML1 thermomechanically rolled thermal
| Property |
Value |
Comment |
| Coefficient of thermal expansion |
Coefficient of thermal expansion of 11.74 1/K |
Predicted Value |
| Specific heat capacity |
Specific heat capacity of 455 J/(kg·K) |
Predicted Value |
| Thermal conductivity |
Thermal conductivity of 38.03 W/(m·K) |
Predicted Value |
EN 10028-5 Grade P355ML1 thermomechanically rolled chemical
| Property |
Value |
Condition |
Related Standards |
Shape |
| Aluminium |
Aluminium of 0.02 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| Carbon |
Carbon of 0.14 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| Manganese |
Manganese of 1.6 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| Molybdenum |
Molybdenum of 0.2 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| Nickel |
Nickel of 0.5 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| Niobium |
Niobium of 0.05 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| Nitrogen |
Nitrogen of 0.015 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| Phosphorus |
Phosphorus of 0.02 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| Silicon |
Silicon of 0.5 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| Sulfur |
Sulfur of 0.008 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| - |
Sulfur of 0.015 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| Titanium |
Titanium of 0.05 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
| Vanadium |
Vanadium of 0.1 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
EN 10028-5 Grade P355ML1 thermomechanically rolled electrical
| Property |
Value |
Comment |
| Electrical conductivity |
Electrical conductivity of 7 S/m |
Predicted Value |
| Electrical resistivity |
Electrical resistivity of 33 Ω·m |
Predicted Value |
EN 10028-5 Grade P355ML1 thermomechanically rolled mechanical
| Property |
Temperature |
Value |
Condition |
Related Standards |
Shape |
Comment |
| Elastic modulus |
- |
Elastic modulus of 190 - 210 GPa |
- |
- |
- |
Typical for Steel |
| Elongation |
- |
Elongation of 17.3 % |
- |
- |
- |
Predicted Value, A200 |
| - |
- |
Elongation of 18.4 % |
- |
- |
- |
Predicted Value, A80 |
| - |
- |
Elongation of 20.3 % |
- |
- |
- |
Predicted Value, A80 Transverse |
| - |
- |
Elongation of 21.1 % |
- |
- |
- |
Predicted Value, A5 |
| - |
- |
Elongation of 21.4 % |
- |
- |
- |
Predicted Value, Transverse |
| - |
- |
Elongation of 22.5 % |
- |
- |
- |
Predicted Value, A50 |
| - |
20 °C |
Elongation of 22 % |
thermomechanically rolled |
EN 10028-5 |
Flat |
- |
| Poisson's ratio |
- |
Poisson's ratio of 0.3 [-] |
- |
- |
- |
Typical for Steel |
| Reduction of area |
- |
Reduction of area of 40.3 % |
- |
- |
- |
Predicted Value |
| - |
- |
Reduction of area of 44.3 % |
- |
- |
- |
Predicted Value, Transverse |
| Shear modulus |
- |
Shear modulus of 79.6 GPa |
- |
- |
- |
Predicted Value |
| Shear strength |
- |
Shear strength of 558.8 MPa |
- |
- |
- |
Predicted Value |
| Tensile strength |
20 °C |
Tensile strength of 450 - 610 MPa |
thermomechanically rolled |
EN 10028-5 |
Flat |
- |
| Yield strength |
- |
Yield strength of 254.6 MPa |
- |
- |
- |
Predicted Value, RP1 |
| - |
- |
Yield strength of 318.5 MPa |
- |
- |
- |
Predicted Value, RP1 Transverse |
| - |
- |
Yield strength of 357.1 MPa |
- |
- |
- |
Predicted Value, RP02 |
| - |
- |
Yield strength of 393.4 MPa |
- |
- |
- |
Predicted Value, Transverse |
| - |
- |
Yield strength of 453.7 MPa |
- |
- |
- |
Predicted Value, RP02 Transverse |
| - |
- |
Yield strength of 468.2 MPa |
- |
- |
- |
Predicted Value, RP05 |
| - |
- |
Yield strength of 494.9 MPa |
- |
- |
- |
Predicted Value, RP002 |
| - |
20 °C |
Yield strength of 345 MPa |
thermomechanically rolled |
EN 10028-5 |
Flat |
- |
| - |
20 °C |
Yield strength of 355 MPa |
thermomechanically rolled |
EN 10028-5 |
Flat |
- |