EN 10025 Grade S275J2C normalized or normalized formed (+N)
EN 10025 Grade S275J2C normalized or normalized formed (+N) introduction
S275J2C is the cold forming grade of the S275J2.
The steel is suited for bending and folding up to thicknesses of 30 mm and suited for roll forming up to 8 mm thickness (minimum values for the radius see Formability - Bending - Folding).
Application: structural steel work
Equivalent material: IS E275, EN S275J2G4C, DIN 1.0142, DIN S275J2G4C, DIN S275J2C, EN 1.0142
EN 10025 Grade S275J2C normalized or normalized formed (+N) general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10025 Grade S275J2C normalized or normalized formed (+N) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
EN 10025 Grade S275J2C normalized or normalized formed (+N) chemical
| Property |
Value |
| Carbon |
Carbon of 0.18 % |
| Copper |
Copper of 0.55 % |
| Manganese |
Manganese of 1.5 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Sulfur |
Sulfur of 0.025 % |
EN 10025 Grade S275J2C normalized or normalized formed (+N) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10025 Grade S275J2C normalized or normalized formed (+N) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
EN 10025 Grade S275J2C normalized or normalized formed (+N) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation |
20.0 °C |
Elongation of 18 - 23 % |
- |
| Elongation A80 |
20.0 °C |
Elongation A80 of 15 - 19 % |
- |
| Elongation A80, transverse |
20.0 °C |
Elongation A80, transverse of 13 - 17 % |
- |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 18 - 21 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 380 - 580 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 195 - 275 MPa |
- |