EN 10025 Grade S235JRC as-rolled condition (+AR)
EN 10025 Grade S235JRC as-rolled condition (+AR) introduction
S235JRC is applicated for moderately loaded construction parts that are not liable to inspection as folding, section cold forming and cold drawing grades. Max. product thickness amounts 20 mm for folding and 8 mm for cold roll forming grades.
Equivalent material: JIS SS330, DIN 1.0122, DIN RQSt 37-2, DIN S235JRC, DIN S235JRG2C, AFNOR S235JRG2, BS S235JRG2, JIS E235B, EN S235JRG2C, EN Fe 360 B, EN 1.0122
EN 10025 Grade S235JRC as-rolled condition (+AR) general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10025 Grade S235JRC as-rolled condition (+AR) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
EN 10025 Grade S235JRC as-rolled condition (+AR) chemical
| Property |
Value |
| Carbon |
Carbon of 0.17 % |
| Manganese |
Manganese of 1.4 % |
| Nitrogen |
Nitrogen of 9E-3 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Sulfur |
Sulfur of 0.045 % |
EN 10025 Grade S235JRC as-rolled condition (+AR) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10025 Grade S235JRC as-rolled condition (+AR) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
EN 10025 Grade S235JRC as-rolled condition (+AR) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation |
20.0 °C |
Elongation of 26 % |
- |
| Elongation A80 |
20.0 °C |
Elongation A80 of 17 - 21 % |
- |
| Elongation A80, transverse |
20.0 °C |
Elongation A80, transverse of 15 - 19 % |
- |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 24 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Yield strength |
20.0 °C |
Yield strength of 225 - 235 MPa |
- |
Create stunning architectural designs with the strength and grace of our steel materials.
-- Our promise