DIN 5512-1 Grade S235JRG2C normalized or normalized formed (+N)
DIN 5512-1 Grade S235JRG2C normalized or normalized formed (+N) introduction
The steel is used for rail vehicle engineering acc. to the selected standard DIN 5512-1.
The corresponding properties of EN 10025-2 shall be taken.
Equivalent material: DIN 1.0122, DIN RQSt 37-2, DIN S235JRC, AFNOR S235JRG2, BS S235JRG2, JIS E235B, EN S235JRC, EN S235JRG2C, EN Fe 360 B, EN 1.0122
DIN 5512-1 Grade S235JRG2C normalized or normalized formed (+N) general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
DIN 5512-1 Grade S235JRG2C normalized or normalized formed (+N) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
DIN 5512-1 Grade S235JRG2C normalized or normalized formed (+N) chemical
| Property |
Value |
| Carbon |
Carbon of 0.17 % |
| Copper |
Copper of 0.55 % |
| Manganese |
Manganese of 1.4 % |
| Nitrogen |
Nitrogen of 0.01 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Sulfur |
Sulfur of 0.035 % |
DIN 5512-1 Grade S235JRG2C normalized or normalized formed (+N) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
DIN 5512-1 Grade S235JRG2C normalized or normalized formed (+N) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
DIN 5512-1 Grade S235JRG2C normalized or normalized formed (+N) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation |
20.0 °C |
Elongation of 21 - 26 % |
- |
| Elongation A80 |
20.0 °C |
Elongation A80 of 17 - 21 % |
- |
| Elongation A80, transverse |
20.0 °C |
Elongation A80, transverse of 17 - 21 % |
- |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 21 - 24 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 340 - 510 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 175 - 235 MPa |
- |
Experience the seamless integration of our steel products into your projects, delivering flawless results every time.
-- Our promise