EN 10025-2 Grade S355J0C as-rolled condition (+AR)
EN 10025-2 Grade S355J0C as-rolled condition (+AR) introduction
S355J0C is used for folding, section cold forming and cold drawing grade. The high-tensile fine grained steel is applicable for welding constructions up to -20 °C subject to the load. Compared to S235J0C is achievable a considerable saving of material due to the by 120 MPa higher yield point. The steel shows a by 15% higher resistance to mineral wear due to sliding action in comparison to S235J0. Max. product thickness amounts 20 mm for folding and 8 mm for cold roll forming grades.
Equivalent material: DIN 1.0554, DIN St 52-3 U, DIN QSt 52-3 U, DIN S355J0C, AFNOR S355J0C, BS S355J0C, EN 1.0554
EN 10025-2 Grade S355J0C as-rolled condition (+AR) general
| Property | Value | Comment |
|---|---|---|
| Density | Density of 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
EN 10025-2 Grade S355J0C as-rolled condition (+AR) thermal
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
| Coefficient of thermal expansion | Coefficient of thermal expansion of 1.32e-05 - 1.38e-05 1/K | - | - | - | Typical for Low Carbon Steel |
| Max service temperature | Max service temperature of -20 °C | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Bar, Sheet, Strip, Flat | Long |
| - | Max service temperature of 500 °C | - | - | - | Typical for Carbon Steel |
| Melting point | Melting point of 1480 - 1526 °C | - | - | - | Typical for Low Carbon Steel |
| Specific heat capacity | Specific heat capacity of 465 J/(kg·K) | - | - | - | Typical for Low Carbon Steel |
| Thermal conductivity | Thermal conductivity of 25 - 93 W/(m·K) | - | - | - | Typical for Low Carbon Steel |
EN 10025-2 Grade S355J0C as-rolled condition (+AR) chemical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Carbon | Carbon of 0.2 % | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Bar, Sheet, Strip, Flat |
| Manganese | Manganese of 1.6 % | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Bar, Sheet, Strip, Flat |
| Nitrogen | Nitrogen of 0.009 % | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Bar, Sheet, Strip, Flat |
| Phosphorus | Phosphorus of 0.04 % | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Bar, Sheet, Strip, Flat |
| Silicon | Silicon of 0.55 % | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Bar, Sheet, Strip, Flat |
| Sulfur | Sulfur of 0.04 % | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Bar, Sheet, Strip, Flat |
EN 10025-2 Grade S355J0C as-rolled condition (+AR) magnetic
| Property | Value | Comment |
|---|---|---|
| Curie temperature | Curie temperature of 770 °C | Typical for Low Carbon Steel |
EN 10025-2 Grade S355J0C as-rolled condition (+AR) electrical
| Property | Value | Comment |
|---|---|---|
| Electrical conductivity | Electrical conductivity of 8 S/m | Predicted Value |
| Electrical resistivity | Electrical resistivity of 1.43e-07 - 1.74e-07 Ω·m | Typical for Carbon Steel |
EN 10025-2 Grade S355J0C as-rolled condition (+AR) mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Elastic modulus | - | Elastic modulus of 200 - 215 GPa | - | - | - | Typical for Low Carbon Steel |
| Elongation | - | Elongation of 17.1 % | - | - | - | Predicted Value, A200 |
| - | - | Elongation of 21.8 % | - | - | - | Predicted Value, A5 |
| - | - | Elongation of 23.2 % | - | - | - | Predicted Value, A50 |
| - | 20 °C | Elongation of 12 % | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Sheet, Strip, Flat | A80 Transverse |
| - | 20 °C | Elongation of 13 % | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Sheet, Strip, Flat | A80 Transverse |
| - | 20 °C | Elongation of 14 % | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Sheet, Strip, Flat | A80 Transverse |
| - | 20 °C | Elongation of 15 % | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Sheet, Strip, Flat | A80 Transverse |
| - | 20 °C | Elongation of 16 % | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Sheet, Strip, Flat | A80 Transverse |
| - | 20 °C | Elongation of 16 % | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Sheet, Strip, Flat | A80 |
| - | 20 °C | Elongation of 17 % | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Sheet, Strip, Flat | A80 |
| - | 20 °C | Elongation of 18 % | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Sheet, Strip, Flat | A80 |
| - | 20 °C | Elongation of 20 % | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Flat, Bar, Sheet, Strip | Transverse |
| - | 20 °C | Elongation of 22 % | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Flat, Bar, Sheet, Strip | - |
| Poisson's ratio | - | Poisson's ratio of 0.29 [-] | - | - | - | Typical for Low Carbon Steel |
| Reduction of area | - | Reduction of area of 41.0 % | - | - | - | Predicted Value |
| - | - | Reduction of area of 43.7 % | - | - | - | Predicted Value, Transverse |
| Shear modulus | - | Shear modulus of 82 GPa | - | - | - | Typical for Low Carbon Steel |
| Shear strength | - | Shear strength of 513.2 MPa | - | - | - | Predicted Value |
| Tensile strength | 20 °C | Tensile strength of 490 - 630 MPa | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Bar, Sheet, Strip, Flat | - |
| - | 20 °C | Tensile strength of 490 - 680 MPa | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Sheet, Strip, Flat | - |
| - | 20 °C | Tensile strength of 510 - 680 MPa | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Sheet, Strip, Flat | - |
| - | 20 °C | Tensile strength of 510 - 630 MPa | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Sheet, Strip, Flat | - |
| Yield strength | - | Yield strength of 254.2 MPa | - | - | - | Predicted Value, RP1 |
| - | - | Yield strength of 316.5 MPa | - | - | - | Predicted Value, RP1 Transverse |
| - | - | Yield strength of 350.6 MPa | - | - | - | Predicted Value, Transverse |
| - | - | Yield strength of 355.9 MPa | - | - | - | Predicted Value, RP02 |
| - | - | Yield strength of 366.5 MPa | - | - | - | Predicted Value, RP05 |
| - | - | Yield strength of 446.5 MPa | - | - | - | Predicted Value, RP02 Transverse |
| - | - | Yield strength of 482.8 MPa | - | - | - | Predicted Value, RP002 |
| - | 20 °C | Yield strength of 345 MPa | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Bar, Sheet, Strip, Flat | - |
| - | 20 °C | Yield strength of 355 MPa | as-rolled condition (+AR) | EN 10025, EN 10025-1, EN 10025-2 | Bar, Sheet, Strip, Flat | - |