EN 10025-2 Grade S185 normalized or normalized formed (+N)
EN 10025-2 Grade S185 normalized or normalized formed (+N) introduction
The hot rolled, unalloyed quality steel S185 is applicated for not strength loaded parts that are not liable to inspection. The chemical composition is not specified.
The steel is not intended for heat treatment. Stress relieving annealing is allowed. Products in the delivery condition +N may be hot formed and/or normalized after delivery.
For long products and continuous rolled flats the delivery condition is up to the producer +AR, +N or +M. The delivery condition of four-high rolled sheet is also up to the producer and may be +AR or +N. Both conditions can be ordered.
Equivalent material: GB Q195, GB U11952, GB U11950, GB U11951, IS Fe290, IS Fe310, IS E165, IS SS330, GOST St0, GOST СT0, KS SS330, ASTM A283 Grade A, UNS K01400, DIN St33, DIN Fe310-0, DIN 1.0035, EN 1.0035, DIN St 33, DIN S185, DIN S185JR, EN S185JR, AFNOR S185, AFNOR A33, UNI Fe320, BS S185, JIS SS330, JIS SGP, JIS SS34, GB/T Q195, GB/T U11952
EN 10025-2 Grade S185 normalized or normalized formed (+N) general
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
| Density | 20 °C | Density of 7.85 g/cm³ | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
EN 10025-2 Grade S185 normalized or normalized formed (+N) thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Coefficient of thermal expansion | -100 °C | Coefficient of thermal expansion of 1.08e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Coefficient of thermal expansion of 1.19e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Coefficient of thermal expansion of 1.25e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Coefficient of thermal expansion of 1.3e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Coefficient of thermal expansion of 1.36e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Coefficient of thermal expansion of 1.41e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Coefficient of thermal expansion of 1.45e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Coefficient of thermal expansion of 1.49e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Max service temperature | - | Max service temperature of 400.7 °C | - | - | - | Predicted Value, Long |
| - | - | Max service temperature of 500 °C | - | - | - | Typical for Carbon Steel |
| Melting point | - | Melting point of 1480 - 1526 °C | - | - | - | Typical for Low Carbon Steel |
| Specific heat capacity | -100 °C | Specific heat capacity of 423 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Specific heat capacity of 461 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Specific heat capacity of 479 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Specific heat capacity of 499 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Specific heat capacity of 517 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Specific heat capacity of 536 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Specific heat capacity of 558 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Specific heat capacity of 587 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Thermal conductivity | 20 °C | Thermal conductivity of 56.9 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Thermal conductivity of 56.4 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Thermal conductivity of 53.5 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Thermal conductivity of 49.4 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Thermal conductivity of 45.2 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Thermal conductivity of 41.3 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Thermal conductivity of 37.6 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Thermal diffusivity | 20 °C | Thermal diffusivity of 15.7 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Thermal diffusivity of 14.5 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Thermal diffusivity of 12.9 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Thermal diffusivity of 11.2 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Thermal diffusivity of 9.6 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Thermal diffusivity of 7.9 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Thermal diffusivity of 6.3 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
EN 10025-2 Grade S185 normalized or normalized formed (+N) magnetic
| Property | Value | Comment |
|---|---|---|
| Curie temperature | Curie temperature of 770 °C | Typical for Low Carbon Steel |
EN 10025-2 Grade S185 normalized or normalized formed (+N) electrical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Electrical conductivity | - | Electrical conductivity of 8 S/m | - | - | - | Predicted Value |
| Electrical resistivity | 20 °C | Electrical resistivity of 1.83e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Electrical resistivity of 2.27e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Electrical resistivity of 2.95e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Electrical resistivity of 3.8e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Electrical resistivity of 4.81e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Electrical resistivity of 5.99e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Electrical resistivity of 7.38e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
EN 10025-2 Grade S185 normalized or normalized formed (+N) mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Elastic modulus | -100 °C | Elastic modulus of 217 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elastic modulus of 212 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Elastic modulus of 207 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Elastic modulus of 199 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Elastic modulus of 192 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Elastic modulus of 184 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Elastic modulus of 175 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Elastic modulus of 164 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Elongation | - | Elongation of 17.9 % | - | - | - | Predicted Value, A200 |
| - | - | Elongation of 22.9 % | - | - | - | Predicted Value, A5 |
| - | - | Elongation of 37.6 % | - | - | - | Predicted Value, A50 |
| - | 20 °C | Elongation of 8 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 9 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 10 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 10 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 11 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 11 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 12 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 12 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 13 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 13 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | Transverse |
| - | 20 °C | Elongation of 14 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 14 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | Transverse |
| - | 20 °C | Elongation of 15 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | Transverse |
| - | 20 °C | Elongation of 15 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elongation of 16 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | Transverse |
| - | 20 °C | Elongation of 16 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elongation of 17 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elongation of 18 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Hardness, Brinell | - | Hardness, Brinell of 268 [-] | - | - | - | Predicted Value, Transverse |
| Poisson's ratio | 20 °C | Poisson's ratio of 0.284 [-] | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Reduction of area | - | Reduction of area of 42.3 % | - | - | - | Predicted Value, Transverse |
| - | - | Reduction of area of 51.8 % | - | - | - | Predicted Value |
| Shear modulus | - | Shear modulus of 82 GPa | - | - | - | Typical for Low Carbon Steel |
| Shear strength | - | Shear strength of 636.4 MPa | - | - | - | Predicted Value |
| Tensile strength | 20 °C | Tensile strength of 270 - 540 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 270 - 510 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 270 - 500 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 270 - 490 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 280 - 540 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 280 - 510 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 280 - 500 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 280 - 490 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 290 - 540 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 290 - 510 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 290 - 500 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 290 - 490 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 310 - 540 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 310 - 510 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 310 - 500 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 310 - 490 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Yield strength | - | Yield strength of 271.7 MPa | - | - | - | Predicted Value, RP1 |
| - | - | Yield strength of 282.3 MPa | - | - | - | Predicted Value, Transverse |
| - | - | Yield strength of 303.2 MPa | - | - | - | Predicted Value, RP05 |
| - | - | Yield strength of 311.9 MPa | - | - | - | Predicted Value, RP1 Transverse |
| - | - | Yield strength of 373.1 MPa | - | - | - | Predicted Value, RP02 |
| - | - | Yield strength of 496.3 MPa | - | - | - | Predicted Value, RP02 Transverse |
| - | - | Yield strength of 500.2 MPa | - | - | - | Predicted Value, RP002 |
| - | 20 °C | Yield strength of 145 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 155 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 165 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 175 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 185 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
We are committed to your success, providing reliable steel solutions that exceed expectations.
-- Our promise
Similar or equivalent steel materials
- EN 10025-2 Grade S235J2 normalized or normalized formed (+N)
- EN 10025-2 Grade S235JR as-rolled condition (+AR)
- EN 10025-2 Grade S235J0 normalized or normalized formed (+N)
- EN 10277-2 Grade St 37-3 cold drawn or turned and soft annealed
- DIN 2393-2 Grade RSt 37-2 bright drawn hard
- DIN 2393-2 Grade RSt 37-2 soft annealed (+A)
- EN 10305-3 Grade RSt 37-2 soft annealed (+A)
- EN 10305-3 Grade RSt 37-2 welded and cold sized
- DIN 2395-3 Grade St 37-3 welded and cold sized
- DIN 2395-3 Grade St 37-3 normalized or normalized formed (+N)
Get a quote