EN 10025-2 Grade E295 normalized or normalized formed (+N)
EN 10025-2 Grade E295 normalized or normalized formed (+N) introduction
E 295 is a general construction steel. It is applicated for wear and strength loaded construction parts (bolts, shafts, spindles, wedges). For this steel is available (mat. No 1.0533) the grade for cold drawing E295GC acc. to DIN EN 10025.
Equivalent material: GB Q275A, GB Q275B, GB U12755, GB U12752, GB Q275, IS Fe490, IS E300, IS SS490, KS SS490, GOST St5ps, GOST St5sp, GOST СT5сп, GOST СT5пс, ASTM A529 Grade 55, ASTM A572 Grade 55, ASTM A573 Grade 70, UNS K02701, DIN St50-2, DIN Fe490-2, NBN A490-2, AFNOR A50-2, GOST S285, IS Fe490-2, UNI Fe490, IS SS50, ÖNORM St490, NP Fe490-2, SS 1550-00, SS 1550-01, UNE A490, UNS K02500, ASTM 50, ASTM 55, DIN 1.0050, EN S295, EN 1.0050, DIN St 50-2, DIN St 50-2 N, DIN E295, AFNOR E295, UNI Fe50, BS E295, JIS SM50YA, JIS SS500, JIS SBPDN930/1080, JIS SBPDN1080/1230, JIS SBPDL1080/1230, JIS SBPDN1275/1420, JIS SBPDL1275/1420, JIS SPFH780, JIS SPFC340BH, ISO Fe490, GB/T Q275, GB/T U12752
EN 10025-2 Grade E295 normalized or normalized formed (+N) general
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
| Density | 20 °C | Density of 7.85 g/cm³ | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire |
EN 10025-2 Grade E295 normalized or normalized formed (+N) thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Coefficient of thermal expansion | -100 °C | Coefficient of thermal expansion of 1.08e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 20 °C | Coefficient of thermal expansion of 1.19e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 100 °C | Coefficient of thermal expansion of 1.25e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 200 °C | Coefficient of thermal expansion of 1.3e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 300 °C | Coefficient of thermal expansion of 1.36e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 400 °C | Coefficient of thermal expansion of 1.41e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 500 °C | Coefficient of thermal expansion of 1.45e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 600 °C | Coefficient of thermal expansion of 1.49e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| Max service temperature | - | Max service temperature of 330.4 °C | - | - | - | Predicted Value, Long |
| - | - | Max service temperature of 500 °C | - | - | - | Typical for Carbon Steel |
| Melting point | - | Melting point of 1480 - 1526 °C | - | - | - | Typical for Low Carbon Steel |
| Specific heat capacity | -100 °C | Specific heat capacity of 423 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 20 °C | Specific heat capacity of 461 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 100 °C | Specific heat capacity of 479 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 200 °C | Specific heat capacity of 499 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 300 °C | Specific heat capacity of 517 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 400 °C | Specific heat capacity of 536 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 500 °C | Specific heat capacity of 558 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 600 °C | Specific heat capacity of 587 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| Thermal conductivity | 20 °C | Thermal conductivity of 53.4 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 100 °C | Thermal conductivity of 52.9 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 200 °C | Thermal conductivity of 50.3 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 300 °C | Thermal conductivity of 46.7 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 400 °C | Thermal conductivity of 43.3 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 500 °C | Thermal conductivity of 39.8 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 600 °C | Thermal conductivity of 36.7 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| Thermal diffusivity | 20 °C | Thermal diffusivity of 14.8 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 100 °C | Thermal diffusivity of 13.6 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 200 °C | Thermal diffusivity of 12.1 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 300 °C | Thermal diffusivity of 10.6 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 400 °C | Thermal diffusivity of 9.2 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 500 °C | Thermal diffusivity of 7.7 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 600 °C | Thermal diffusivity of 6.2 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
EN 10025-2 Grade E295 normalized or normalized formed (+N) chemical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Nitrogen | Nitrogen of 0.012 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire |
| Phosphorus | Phosphorus of 0.045 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire |
| Sulfur | Sulfur of 0.045 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire |
EN 10025-2 Grade E295 normalized or normalized formed (+N) magnetic
| Property | Value | Comment |
|---|---|---|
| Curie temperature | Curie temperature of 770 °C | Typical for Low Carbon Steel |
EN 10025-2 Grade E295 normalized or normalized formed (+N) electrical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Electrical conductivity | - | Electrical conductivity of 8 S/m | - | - | - | Predicted Value |
| Electrical resistivity | 20 °C | Electrical resistivity of 1.95e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 100 °C | Electrical resistivity of 2.42e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 200 °C | Electrical resistivity of 3.14e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 300 °C | Electrical resistivity of 4.02e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 400 °C | Electrical resistivity of 5.02e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 500 °C | Electrical resistivity of 6.21e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 600 °C | Electrical resistivity of 7.55e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
EN 10025-2 Grade E295 normalized or normalized formed (+N) mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Elastic modulus | -100 °C | Elastic modulus of 217 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 20 °C | Elastic modulus of 212 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 100 °C | Elastic modulus of 207 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 200 °C | Elastic modulus of 199 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 300 °C | Elastic modulus of 192 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 400 °C | Elastic modulus of 184 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 500 °C | Elastic modulus of 175 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| - | 600 °C | Elastic modulus of 164 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| Elongation | - | Elongation of 14.3 % | - | - | - | Predicted Value, A200 |
| - | - | Elongation of 19.1 % | - | - | - | Predicted Value, A50 |
| - | - | Elongation of 20.9 % | - | - | - | Predicted Value, A5 |
| - | 20 °C | Elongation of 10 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 11 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 12 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 12 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 13 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 13 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 14 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 14 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | Transverse |
| - | 20 °C | Elongation of 14 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 15 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | Transverse |
| - | 20 °C | Elongation of 15 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 15 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elongation of 16 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | Transverse |
| - | 20 °C | Elongation of 16 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 16 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elongation of 17 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | Transverse |
| - | 20 °C | Elongation of 18 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | Transverse |
| - | 20 °C | Elongation of 18 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elongation of 19 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elongation of 20 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | - |
| Hardness, Brinell | - | Hardness, Brinell of 270 [-] | - | - | - | Predicted Value, Transverse |
| Poisson's ratio | 20 °C | Poisson's ratio of 0.284 [-] | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Sheet, Strip, Flat, Rod, Wire | - |
| Reduction of area | - | Reduction of area of 41.4 % | - | - | - | Predicted Value |
| - | - | Reduction of area of 42.5 % | - | - | - | Predicted Value, Transverse |
| Shear modulus | - | Shear modulus of 82 GPa | - | - | - | Typical for Low Carbon Steel |
| Shear strength | - | Shear strength of 552.2 MPa | - | - | - | Predicted Value |
| Tensile strength | 20 °C | Tensile strength of 440 - 660 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 440 - 610 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 450 - 660 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 450 - 610 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 470 - 660 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 470 - 610 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 490 - 660 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 490 - 610 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | - |
| Yield strength | - | Yield strength of 307 MPa | - | - | - | Predicted Value, RP1 Transverse |
| - | - | Yield strength of 311.3 MPa | - | - | - | Predicted Value, RP1 |
| - | - | Yield strength of 326.4 MPa | - | - | - | Predicted Value, RP05 |
| - | - | Yield strength of 401.4 MPa | - | - | - | Predicted Value, Transverse |
| - | - | Yield strength of 498.6 MPa | - | - | - | Predicted Value, RP02 Transverse |
| - | - | Yield strength of 523.8 MPa | - | - | - | Predicted Value, RP02 |
| - | - | Yield strength of 619.6 MPa | - | - | - | Predicted Value, RP002 |
| - | 20 °C | Yield strength of 225 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 235 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 245 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 255 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 265 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 275 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 285 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 295 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025, EN 10025-1 | Strip, Sheet, Flat, Rod, Wire | - |
Our steel products are engineered to deliver long-lasting performance, offering an excellent return on investment.
-- Our promise
Similar or equivalent steel materials
- EN 10025-2 Grade S355JR normalized or normalized formed (+N)
- EN 10277-2 Grade St 50-2 cold drawn
- EN 10277-2 Grade St 50-2 cold drawn or turned and normalized
- EN 10277-2 Grade St 50-2 turned
- EN 10277-2 Grade St 50-2 cold drawn or turned and soft annealed
- DIN 17240 Grade C35 quenched and tempered (+QT)
- DIN 17240 Grade Ck 35 quenched and tempered (+QT)
- DIN 17240 Grade C 35 normalized or normalized formed (+N)
- JIS G3444 Grade STK490
- JIS G3106 Grade SM490B