EN 10016-3 Grade C2D1
EN 10016-3 Grade C2D1 introduction
Steel wire rod of low carbon, low silicon, rimmed and rimmed substitute steel with high ductility for drawing and/or cold rolling
Equivalent material: ISO C2D1, GB C2D1, DIN 1.1185, DIN C2D1, AFNOR C2D1, BS C2D1, JIS SPP, EN 1.1185, GB/T C2D1
EN 10016-3 Grade C2D1 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10016-3 Grade C2D1 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
EN 10016-3 Grade C2D1 chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.01 % |
| Carbon |
Carbon of 0.03 % |
| Chromium |
Chromium of 0.1 % |
| Copper |
Copper of 0.1 % |
| Manganese |
Manganese of 0.1 - 0.35 % |
| Molybdenum |
Molybdenum of 0.03 % |
| Nickel |
Nickel of 0.1 % |
| Nitrogen |
Nitrogen of 7E-3 % |
| Phosphorus |
Phosphorus of 0.02 % |
| Silicon |
Silicon of 0.05 % |
| Sulfur |
Sulfur of 0.02 % |
EN 10016-3 Grade C2D1 magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10016-3 Grade C2D1 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
EN 10016-3 Grade C2D1 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |