DIN 5512-1 Grade S355J2G3C normalized or normalized formed (+N)
DIN 5512-1 Grade S355J2G3C normalized or normalized formed (+N) introduction
The steel is used for rail vehicle engineering acc. to the selected standard DIN 5512-1.
The corresponding properties of EN 10025-2 shall be taken.
Equivalent material: DIN QSt52-3N, DIN 1.0569, DIN St 52-3 N, DIN QSt 52-3, DIN S355J2C, BS 50 D8, EN S355J2G3, EN 1.0569
DIN 5512-1 Grade S355J2G3C normalized or normalized formed (+N) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
DIN 5512-1 Grade S355J2G3C normalized or normalized formed (+N) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.11E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.21E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.29E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.35E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 54 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 50.7 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 46.9 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 41.5 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 39.4 W/(m·K) |
- |
DIN 5512-1 Grade S355J2G3C normalized or normalized formed (+N) chemical
| Property |
Value |
| Carbon |
Carbon of 0.2 % |
| Manganese |
Manganese of 1.6 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.55 % |
| Sulfur |
Sulfur of 0.035 % |
DIN 5512-1 Grade S355J2G3C normalized or normalized formed (+N) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
DIN 5512-1 Grade S355J2G3C normalized or normalized formed (+N) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 2E-7 Ω·m |
DIN 5512-1 Grade S355J2G3C normalized or normalized formed (+N) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 210 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 205 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 195 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 185 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 175 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 22 % |
- |
| Elongation A80 |
20.0 °C |
Elongation A80 of 14 - 18 % |
- |
| Elongation A80, transverse |
20.0 °C |
Elongation A80, transverse of 12 - 16 % |
- |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 20 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 490 - 680 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 345 - 355 MPa |
- |
Our stringent quality control measures ensure consistent and reliable steel products.
-- Our promise