DIN 2393-2 Grade St37-2 bright drawn hard

DIN 2393-2 Grade St37-2 bright drawn hard

Equivalent material: EN S235JR+CR, DIN 1.0401, DIN St 37-2 G, DIN St 37, DIN St37-2, DIN C15, AFNOR CC12, BS 080M15, UNI C15C16, SS 1350, UNE F.111, AISI 1015, AISI 1017, AISI 1016, SAE 1015, SAE 1017, SAE 1016, JIS S15C, EN C15, EN 1.0401, ASTM M1015, ASTM Grade 1015, UNS G10150, UNS G10170

DIN 2393-2 Grade St37-2 bright drawn hard general

Property Temperature Value
Density 20.0 °C Density of 7.85 g/cm³

DIN 2393-2 Grade St37-2 bright drawn hard thermal

Property Temperature Value Comment
Coefficient of thermal expansion -100.0 °C Coefficient of thermal expansion of 1.08E-5 1/K -
- 20.0 °C Coefficient of thermal expansion of 1.19E-5 1/K -
- 100.0 °C Coefficient of thermal expansion of 1.25E-5 1/K -
- 200.0 °C Coefficient of thermal expansion of 1.3E-5 1/K -
- 300.0 °C Coefficient of thermal expansion of 1.36E-5 1/K -
- 400.0 °C Coefficient of thermal expansion of 1.41E-5 1/K -
- 500.0 °C Coefficient of thermal expansion of 1.45E-5 1/K -
- 600.0 °C Coefficient of thermal expansion of 1.49E-5 1/K -
Max service temperature - Max service temperature of 500 °C Typical for Carbon Steel
Melting point - Melting point of 1480 - 1526 °C Typical for Low Carbon Steel
Specific heat capacity -100.0 °C Specific heat capacity of 423 J/(kg·K) -
- 20.0 °C Specific heat capacity of 461 J/(kg·K) -
- 100.0 °C Specific heat capacity of 479 J/(kg·K) -
- 200.0 °C Specific heat capacity of 499 J/(kg·K) -
- 300.0 °C Specific heat capacity of 517 J/(kg·K) -
- 400.0 °C Specific heat capacity of 536 J/(kg·K) -
- 500.0 °C Specific heat capacity of 558 J/(kg·K) -
- 600.0 °C Specific heat capacity of 587 J/(kg·K) -
Thermal conductivity 20.0 °C Thermal conductivity of 56.9 W/(m·K) -
- 100.0 °C Thermal conductivity of 56.4 W/(m·K) -
- 200.0 °C Thermal conductivity of 53.5 W/(m·K) -
- 300.0 °C Thermal conductivity of 49.4 W/(m·K) -
- 400.0 °C Thermal conductivity of 45.2 W/(m·K) -
- 500.0 °C Thermal conductivity of 41.3 W/(m·K) -
- 600.0 °C Thermal conductivity of 37.6 W/(m·K) -
Thermal diffusivity 20.0 °C Thermal diffusivity of 15.7 mm²/s -
- 100.0 °C Thermal diffusivity of 14.5 mm²/s -
- 200.0 °C Thermal diffusivity of 12.9 mm²/s -
- 300.0 °C Thermal diffusivity of 11.2 mm²/s -
- 400.0 °C Thermal diffusivity of 9.6 mm²/s -
- 500.0 °C Thermal diffusivity of 7.9 mm²/s -
- 600.0 °C Thermal diffusivity of 6.3 mm²/s -

DIN 2393-2 Grade St37-2 bright drawn hard chemical

Property Value
Carbon Carbon of 0.17 %
Phosphorus Phosphorus of 0.05 %
Sulfur Sulfur of 0.05 %

DIN 2393-2 Grade St37-2 bright drawn hard magnetic

Property Value Comment
Curie temperature Curie temperature of 770 °C Typical for Low Carbon Steel

DIN 2393-2 Grade St37-2 bright drawn hard electrical

Property Temperature Value
Electrical resistivity 20.0 °C Electrical resistivity of 1.83E-7 Ω·m
- 100.0 °C Electrical resistivity of 2.27E-7 Ω·m
- 200.0 °C Electrical resistivity of 2.95E-7 Ω·m
- 300.0 °C Electrical resistivity of 3.8E-7 Ω·m
- 400.0 °C Electrical resistivity of 4.81E-7 Ω·m
- 500.0 °C Electrical resistivity of 5.99E-7 Ω·m
- 600.0 °C Electrical resistivity of 7.38E-7 Ω·m

DIN 2393-2 Grade St37-2 bright drawn hard mechanical

Property Temperature Value Comment
Elastic modulus -100.0 °C Elastic modulus of 217 GPa -
- 20.0 °C Elastic modulus of 212 GPa -
- 100.0 °C Elastic modulus of 207 GPa -
- 200.0 °C Elastic modulus of 199 GPa -
- 300.0 °C Elastic modulus of 192 GPa -
- 400.0 °C Elastic modulus of 184 GPa -
- 500.0 °C Elastic modulus of 175 GPa -
- 600.0 °C Elastic modulus of 164 GPa -
Elongation 20.0 °C Elongation of 6 % -
Poisson's ratio 20.0 °C Poisson's ratio of 0.28 [-] -
Shear modulus 23.0 °C Shear modulus of 82 GPa Typical for Low Carbon Steel
Tensile strength 20.0 °C Tensile strength of 440 MPa -