DIN 17212 Grade Cf53 normalized or normalized formed (+N)
DIN 17212 Grade Cf53 normalized or normalized formed (+N) introduction
The in the quenched and tempered condition flame and induction hardenable unalloyed special steel has a, compared to the common quenched and tempered steel, constricted range of the C content and a lower maximum value of the P content.
The steel is suitable for flash welding, if prooved conditions will be kept.
For better machining the steel can be soft annealed. In this soft annealed and also in the normalised condition the material is unrestrained cold shearable.
A maximum value for nonmetallic inclusions by arrangement.
Delivery forms:
- semi-finished product, rolled or forged
- steel bars, hot-rolled or hot forged
- wire, hot-rolled
- sheet, strip and wide flats, hot-rolled
- tubes, coils, seamless
- open die and drop forgings
Application:
car industry, engine construction, mechanical engineering
Equivalent material: ISO 5, DIN 1.1213, DIN C53G, DIN Cf 53, DIN C53E, AFNOR XC48TS, UNI C53, SS 1674, AISI 1050, AISI 1055, SAE 1050, SAE 1055, JIS S50C, JIS S50CM, EN C53G, EN 1.1213, ISO S50C, UNS G10500, UNS G10550, IS 55C6
DIN 17212 Grade Cf53 normalized or normalized formed (+N) general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Medium Carbon Steel |
DIN 17212 Grade Cf53 normalized or normalized formed (+N) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
Typical for Medium Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1380 - 1514 °C |
Typical for Medium Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 470 - 520 J/(kg·K) |
Typical for Medium Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 21 - 52 W/(m·K) |
Typical for Medium Carbon Steel |
DIN 17212 Grade Cf53 normalized or normalized formed (+N) chemical
| Property |
Value |
| Carbon |
Carbon of 0.5 - 0.57 % |
| Manganese |
Manganese of 0.4 - 0.7 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.35 % |
| Sulfur |
Sulfur of 0.035 % |
DIN 17212 Grade Cf53 normalized or normalized formed (+N) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
DIN 17212 Grade Cf53 normalized or normalized formed (+N) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Medium Carbon Steel |
| Elongation |
20.0 °C |
Elongation of 16 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Medium Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 75 - 80 GPa |
Typical for Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 610 - 760 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 340 MPa |
- |
Experience the seamless integration of our steel products into your projects, delivering flawless results every time.