EN 10277-5 Grade C50E cold drawn
EN 10277-5 Grade C50E cold drawn introduction
Steel C50E is suitable for larger parts (heavy forged parts) in vehicle, engine and machine engineering (e.g. transmission parts, shafts, wheel hubs). Lowest application temperature -25°C.
As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).
Equivalent material: GB 50, BS 080M50, ISO C50E4, UNI C50, JIS S50C, SS 1674, ASTM 1050, DIN Ck50, GB U20502, ISO C50E, ASTM A108 Grade 1050, SAE 1050, UNS G10500, DIN 1.1206, DIN C50E, AFNOR C50E, AFNOR XC50, BS En43A, BS C50E, BS 50CS, BS 50HS, BS CS50, AISI 1049, AISI 1050, SAE 1049, JIS S53C, EN 1.1206, GOST 50, GB SM50, GB T10500, GB/T 50, GB/T U20502, GB/T SM50, GB/T T10500, ASTM Grade 1050, UNS G10490
EN 10277-5 Grade C50E cold drawn general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.8 - 7.85 g/cm³ |
EN 10277-5 Grade C50E cold drawn thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.11E-5 - 1.25E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.21E-5 - 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.29E-5 - 1.36E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.35E-5 - 1.41E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Max service temperature, long |
- |
Max service temperature, long of -25 - 0 °C |
- |
| Melting point |
- |
Melting point of 1380 - 1514 °C |
Typical for Medium Carbon Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 460 - 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 41.7 - 52 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 43.4 - 50.6 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 43.2 - 48.1 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 41.4 - 45.7 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 39.1 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 36.7 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 34.1 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 11.6 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 11.3 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 10.5 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 9.5 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.3 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.1 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 5.8 mm²/s |
- |
EN 10277-5 Grade C50E cold drawn chemical
| Property |
Value |
| Carbon |
Carbon of 0.47 - 0.55 % |
| Chromium |
Chromium of 0.4 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Molybdenum |
Molybdenum of 0.1 % |
| Nickel |
Nickel of 0.4 % |
| Phosphorus |
Phosphorus of 0.03 - 0.04 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.035 % |
EN 10277-5 Grade C50E cold drawn electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.2E-7 - 2.5E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.95E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.65E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.53E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.56E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.74E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 8.13E-7 Ω·m |
EN 10277-5 Grade C50E cold drawn mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 210 - 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 205 - 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 195 - 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 185 - 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 175 - 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 5 - 8 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Medium Carbon Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 650 - 1100 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 390 - 590 MPa |
- |