DIN 17210 Grade Ck15 soft annealed (+A)
DIN 17210 Grade Ck15 soft annealed (+A) introduction
The steel Ck 15 is used for increased wear loaded parts with higher core strength in the vehicle and mechanical engineering as well as for parts of larger dimension and complexer shape as the base grade C 15 (e.g. levers, joints, gears).
The lowest application amounts to -25 °C.
Equivalent material: NBN C16-2, CSN 12020, AFNOR XC12, BS 080M15, GOST 15, ISO C15E4, UNI 2C15, JIS S15C, SS 1370-04, VSM CK15, UNE F.1511-C16K, ASTM 1015, DIN C15E, DIN 1.1141, AFNOR C15E, AFNOR XC18, AFNOR C18RR, AFNOR XC15, BS C15E, BS En32C, BS 080A15, UNI C16, SS 1370, UNE C15K, AISI 1015, AISI 1017, SAE 1015, SAE 1017, JIS S15CK, EN C15E, EN 1.1141, ISO C15E, ISO S15C, GB/T 15, GB/T U20152, ASTM M1015, ASTM Grade 1015, UNS G10170, UNS G10150
DIN 17210 Grade Ck15 soft annealed (+A) general
Property |
Temperature |
Value |
Density |
20.0 °C |
Density of 7.85 g/cm³ |
DIN 17210 Grade Ck15 soft annealed (+A) thermal
Property |
Temperature |
Value |
Comment |
Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
- |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
- |
100.0 °C |
Coefficient of thermal expansion of 1.1E-5 - 1.25E-5 1/K |
- |
- |
200.0 °C |
Coefficient of thermal expansion of 1.18E-5 - 1.3E-5 1/K |
- |
- |
300.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
- |
400.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.41E-5 1/K |
- |
- |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
- |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
Max service temperature, long |
- |
Max service temperature, long of -25 - 0 °C |
- |
Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
- |
20.0 °C |
Specific heat capacity of 460 - 461 J/(kg·K) |
- |
- |
100.0 °C |
Specific heat capacity of 479 - 480 J/(kg·K) |
- |
- |
200.0 °C |
Specific heat capacity of 499 - 520 J/(kg·K) |
- |
- |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
- |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
- |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
- |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
Thermal conductivity |
20.0 °C |
Thermal conductivity of 57.5 - 58.7 W/(m·K) |
- |
- |
100.0 °C |
Thermal conductivity of 54.4 - 55.7 W/(m·K) |
- |
- |
200.0 °C |
Thermal conductivity of 50.2 - 51.9 W/(m·K) |
- |
- |
300.0 °C |
Thermal conductivity of 47.6 W/(m·K) |
- |
- |
400.0 °C |
Thermal conductivity of 43.4 - 44 W/(m·K) |
- |
- |
500.0 °C |
Thermal conductivity of 39.6 W/(m·K) |
- |
- |
600.0 °C |
Thermal conductivity of 36 W/(m·K) |
- |
Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 15.9 mm²/s |
- |
- |
100.0 °C |
Thermal diffusivity of 14.3 mm²/s |
- |
- |
200.0 °C |
Thermal diffusivity of 12.5 mm²/s |
- |
- |
300.0 °C |
Thermal diffusivity of 10.8 mm²/s |
- |
- |
400.0 °C |
Thermal diffusivity of 9.2 mm²/s |
- |
- |
500.0 °C |
Thermal diffusivity of 7.6 mm²/s |
- |
- |
600.0 °C |
Thermal diffusivity of 6.1 mm²/s |
- |
DIN 17210 Grade Ck15 soft annealed (+A) chemical
Property |
Value |
Carbon |
Carbon of 0.12 - 0.18 % |
Manganese |
Manganese of 0.3 - 0.6 % |
Phosphorus |
Phosphorus of 0.04 % |
Silicon |
Silicon of 0.4 % |
Sulfur |
Sulfur of 0.035 % |
DIN 17210 Grade Ck15 soft annealed (+A) magnetic
Property |
Value |
Comment |
Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
DIN 17210 Grade Ck15 soft annealed (+A) electrical
Property |
Temperature |
Value |
Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.1E-7 Ω·m |
- |
100.0 °C |
Electrical resistivity of 2.3E-7 Ω·m |
- |
200.0 °C |
Electrical resistivity of 3.04E-7 Ω·m |
- |
300.0 °C |
Electrical resistivity of 3.94E-7 Ω·m |
- |
400.0 °C |
Electrical resistivity of 5.01E-7 Ω·m |
- |
500.0 °C |
Electrical resistivity of 6.25E-7 Ω·m |
- |
600.0 °C |
Electrical resistivity of 7.7E-7 Ω·m |
DIN 17210 Grade Ck15 soft annealed (+A) mechanical
Property |
Temperature |
Value |
Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
20.0 °C |
Elastic modulus of 210 - 212 GPa |
- |
100.0 °C |
Elastic modulus of 205 - 207 GPa |
- |
200.0 °C |
Elastic modulus of 193 - 199 GPa |
- |
300.0 °C |
Elastic modulus of 185 - 192 GPa |
- |
400.0 °C |
Elastic modulus of 175 - 184 GPa |
- |
500.0 °C |
Elastic modulus of 175 GPa |
- |
600.0 °C |
Elastic modulus of 164 GPa |
Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.28 [-] |
Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |