DIN 17173 Grade 10Ni14 quenched and tempered (+QT)
Equivalent material: EN 12Ni14, DIN 1.5637, DIN 12Ni14, BS 12Ni14, JIS STBL450, JIS SL3N255, JIS SL3N275, JIS SL3N440, JIS STPL450, EN 14Ni14, EN 1.5637, ISO 13Ni14, ASTM Grade D, ASTM Grade LF3 Class 1
DIN 17173 Grade 10Ni14 quenched and tempered (+QT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
DIN 17173 Grade 10Ni14 quenched and tempered (+QT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.02E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.13E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.18E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.23E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.27E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.31E-5 1/K |
- |
| Melting point |
- |
Melting point of 1316 - 1595 °C |
Typical for Nickel Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 441 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 464 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 496 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 513 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 532 J/(kg·K) |
- |
| Thermal conductivity |
-100.0 °C |
Thermal conductivity of 28.9 W/(m·K) |
- |
| - |
20.0 °C |
Thermal conductivity of 35.8 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 38.1 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 38.9 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 38 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 36.8 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 9.8 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 9.9 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 9.5 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 8.7 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 7.8 mm²/s |
- |
DIN 17173 Grade 10Ni14 quenched and tempered (+QT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.15 % |
| Manganese |
Manganese of 0.3 - 0.8 % |
| Nickel |
Nickel of 3.25 - 3.75 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.35 % |
| Sulfur |
Sulfur of 0.02 % |
| Vanadium |
Vanadium of 0.05 % |
DIN 17173 Grade 10Ni14 quenched and tempered (+QT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
-100.0 °C |
Electrical resistivity of 2E-7 Ω·m |
| - |
20.0 °C |
Electrical resistivity of 2.65E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 3.14E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.79E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.61E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.51E-7 Ω·m |
DIN 17173 Grade 10Ni14 quenched and tempered (+QT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 214 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 207 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 202 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 196 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 189 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 181 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 20 % |
- |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 18 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Nickel Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 76 GPa |
Typical for Nickel Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 470 - 640 MPa |
- |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 470 - 640 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 335 - 345 MPa |
- |
| Yield strength, transverse |
20.0 °C |
Yield strength, transverse of 335 - 345 MPa |
- |
Trust our exceptional steel products to inspire confidence in your projects.