DIN 17140-1 Grade D95-2
DIN 17140-1 Grade D95-2 introduction
Non-alloy steel wire rod for cold drawing for general purpose rod
Equivalent material: GB C92D, GB U53922, IS nan, ASTM 1095, UNS G10950, SAE 1095, DIN 1.0618, DIN C92D, AFNOR C92D, BS 95HS, BS C92D, BS 95CS, AISI 1095, AISI 1090, SAE 1090, JIS CS95, EN C92D, EN 1.0618, ISO CS95, ISO C92D, GB/T C92D, GB/T U53922, UNS G10900
DIN 17140-1 Grade D95-2 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for High Carbon Steel |
DIN 17140-1 Grade D95-2 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
Typical for High Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 486 J/(kg·K) |
Typical for High Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 W/(m·K) |
Typical for High Carbon Steel |
DIN 17140-1 Grade D95-2 chemical
| Property |
Value |
| Carbon |
Carbon of 0.9 - 0.99 % |
| Manganese |
Manganese of 0.3 - 0.7 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.1 - 0.3 % |
| Sulfur |
Sulfur of 0.04 % |
DIN 17140-1 Grade D95-2 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
DIN 17140-1 Grade D95-2 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for High Carbon Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 81 GPa |
Typical for High Carbon Steel |