EN 10132-4 Grade C100S quenched and tempered (+QT)
EN 10132-4 Grade C100S quenched and tempered (+QT) introduction
The steel C100S is used as cold rolled strip for springs and special applications in thicknesses of up to 6 mm and as tempered cold strip in thicknesses from 0.30 to 3.00 mm. The springs made of steel C100S are suitable for highly stressed tension springs, especially in the watch industry, as well as for pen nibs.
Equivalent material: IS 98C6, IS 8, JIS SK95-CSP, ASTM A684 Grade 1095, AISI 1095, ASTM G10950, DIN Ck101, DIN 1.1274, DIN C100S, AFNOR C100S, AFNOR XC100, AFNOR C100RR, BS C100S, BS 95, SAE 1095, JIS SK4, EN 1.1274, ISO CS95, ASTM 1095, UNS G10950
EN 10132-4 Grade C100S quenched and tempered (+QT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.8 g/cm³ |
EN 10132-4 Grade C100S quenched and tempered (+QT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.25E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.41E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 41.7 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 43.4 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 43.2 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 41.4 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 39.1 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 36.7 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 34.1 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 11.6 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 11.3 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 10.5 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 9.5 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.3 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.1 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 5.8 mm²/s |
- |
EN 10132-4 Grade C100S quenched and tempered (+QT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.95 - 1.05 % |
| Chromium |
Chromium of 0.4 % |
| Manganese |
Manganese of 0.3 - 0.6 % |
| Molybdenum |
Molybdenum of 0.1 % |
| Nickel |
Nickel of 0.4 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.35 % |
| Sulfur |
Sulfur of 0.025 % |
EN 10132-4 Grade C100S quenched and tempered (+QT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 2.5E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.95E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.65E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.53E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.56E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.74E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 8.13E-7 Ω·m |
EN 10132-4 Grade C100S quenched and tempered (+QT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Hardness, Rockwell C |
20.0 °C |
Hardness, Rockwell C of 38.5 - 57 [-] |
- |
| Hardness, Vickers |
20.0 °C |
Hardness, Vickers of 370 - 630 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 81 GPa |
Typical for High Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 1200 - 2100 MPa |
- |