DIN 17111 Grade USt36 hot rolled
DIN 17111 Grade USt36 hot rolled introduction
The steel is used for the manufacture of bolts, nuts and rivets (and similar shaped parts).
Equivalent material: IS 1148, JIS SV34, JIS SV330, DIN 1.0203, EN 1.0203
DIN 17111 Grade USt36 hot rolled general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.85 g/cm³ |
DIN 17111 Grade USt36 hot rolled thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | -100.0 °C | Coefficient of thermal expansion of 1.08E-5 1/K | - |
| - | 20.0 °C | Coefficient of thermal expansion of 1.19E-5 1/K | - |
| - | 100.0 °C | Coefficient of thermal expansion of 1.25E-5 1/K | - |
| - | 200.0 °C | Coefficient of thermal expansion of 1.3E-5 1/K | - |
| - | 300.0 °C | Coefficient of thermal expansion of 1.36E-5 1/K | - |
| - | 400.0 °C | Coefficient of thermal expansion of 1.41E-5 1/K | - |
| - | 500.0 °C | Coefficient of thermal expansion of 1.45E-5 1/K | - |
| - | 600.0 °C | Coefficient of thermal expansion of 1.49E-5 1/K | - |
| Max service temperature | - | Max service temperature of 500 °C | Typical for Carbon Steel |
| Melting point | - | Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
| Specific heat capacity | -100.0 °C | Specific heat capacity of 423 J/(kg·K) | - |
| - | 20.0 °C | Specific heat capacity of 461 J/(kg·K) | - |
| - | 100.0 °C | Specific heat capacity of 479 J/(kg·K) | - |
| - | 200.0 °C | Specific heat capacity of 499 J/(kg·K) | - |
| - | 300.0 °C | Specific heat capacity of 517 J/(kg·K) | - |
| - | 400.0 °C | Specific heat capacity of 536 J/(kg·K) | - |
| - | 500.0 °C | Specific heat capacity of 558 J/(kg·K) | - |
| - | 600.0 °C | Specific heat capacity of 587 J/(kg·K) | - |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 56.9 W/(m·K) | - |
| - | 100.0 °C | Thermal conductivity of 56.4 W/(m·K) | - |
| - | 200.0 °C | Thermal conductivity of 53.5 W/(m·K) | - |
| - | 300.0 °C | Thermal conductivity of 49.4 W/(m·K) | - |
| - | 400.0 °C | Thermal conductivity of 45.2 W/(m·K) | - |
| - | 500.0 °C | Thermal conductivity of 41.3 W/(m·K) | - |
| - | 600.0 °C | Thermal conductivity of 37.6 W/(m·K) | - |
| Thermal diffusivity | 20.0 °C | Thermal diffusivity of 15.7 mm²/s | - |
| - | 100.0 °C | Thermal diffusivity of 14.5 mm²/s | - |
| - | 200.0 °C | Thermal diffusivity of 12.9 mm²/s | - |
| - | 300.0 °C | Thermal diffusivity of 11.2 mm²/s | - |
| - | 400.0 °C | Thermal diffusivity of 9.6 mm²/s | - |
| - | 500.0 °C | Thermal diffusivity of 7.9 mm²/s | - |
| - | 600.0 °C | Thermal diffusivity of 6.3 mm²/s | - |
DIN 17111 Grade USt36 hot rolled chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.14 % |
| Manganese | Manganese of 0.25 - 0.5 % |
| Phosphorus | Phosphorus of 0.05 % |
| Sulfur | Sulfur of 0.05 % |
DIN 17111 Grade USt36 hot rolled magnetic
| Property | Value | Comment |
|---|---|---|
| Curie temperature | Curie temperature of 770 °C | Typical for Low Carbon Steel |
DIN 17111 Grade USt36 hot rolled electrical
| Property | Temperature | Value |
|---|---|---|
| Electrical resistivity | 20.0 °C | Electrical resistivity of 1.83E-7 Ω·m |
| - | 100.0 °C | Electrical resistivity of 2.27E-7 Ω·m |
| - | 200.0 °C | Electrical resistivity of 2.95E-7 Ω·m |
| - | 300.0 °C | Electrical resistivity of 3.8E-7 Ω·m |
| - | 400.0 °C | Electrical resistivity of 4.81E-7 Ω·m |
| - | 500.0 °C | Electrical resistivity of 5.99E-7 Ω·m |
| - | 600.0 °C | Electrical resistivity of 7.38E-7 Ω·m |
DIN 17111 Grade USt36 hot rolled mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | -100.0 °C | Elastic modulus of 217 GPa | - |
| - | 20.0 °C | Elastic modulus of 212 GPa | - |
| - | 100.0 °C | Elastic modulus of 207 GPa | - |
| - | 200.0 °C | Elastic modulus of 199 GPa | - |
| - | 300.0 °C | Elastic modulus of 192 GPa | - |
| - | 400.0 °C | Elastic modulus of 184 GPa | - |
| - | 500.0 °C | Elastic modulus of 175 GPa | - |
| - | 600.0 °C | Elastic modulus of 164 GPa | - |
| Elongation | 20.0 °C | Elongation of 30 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.29 [-] | Typical for Low Carbon Steel |
| Shear modulus | 23.0 °C | Shear modulus of 82 GPa | Typical for Low Carbon Steel |
| Tensile strength | 20.0 °C | Tensile strength of 330 - 430 MPa | - |
| Yield strength | 20.0 °C | Yield strength of 195 - 205 MPa | - |
Collaborate with us to bring your vision to life using our premium-grade steel materials.
-- Our promise
Similar or equivalent steel materials
- EN 10025-3 Grade S420N normalized or normalized formed (+N)
- EN 10217-3 Grade StE 420 normalized or normalized formed (+N)
- EN 10217-3 Grade TStE 420 normalized or normalized formed (+N)
- DIN 17125 Grade TStE 420 normalized or normalized formed (+N)
- DIN 17125 Grade StE 420 normalized or normalized formed (+N)
- DIN 17111 Grade RSt36 hot rolled
- DIN 17111 Grade RSt38 hot rolled
- DIN 17111 Grade UQSt 36 hot rolled
- DIN 17111 Grade UQSt38 hot rolled
- DIN 17111 Grade USt38 hot rolled