DIN 1652-3 Grade 22CrMoS3-5 cold drawn or turned and soft annealed
DIN 1652-3 Grade 22CrMoS3-5 cold drawn or turned and soft annealed introduction
The steel 22 CrMoS 3 5 is used for wear loaded parts in the vehicle and mechanical engineering with medium core strength, better machinability, high toughness and high fatigue strength (e.g. gears, shafts, axles).
The lowest application amounts to -60 °C, the best application up to 60 mm nominal size.
Equivalent material: DIN 1.7333, EN 22CrMoS3-5, EN 1.7333, ASTM G41210, UNS G41210
DIN 1652-3 Grade 22CrMoS3-5 cold drawn or turned and soft annealed general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.83 g/cm³ |
DIN 1652-3 Grade 22CrMoS3-5 cold drawn or turned and soft annealed thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | -100.0 °C | Coefficient of thermal expansion of 1.05E-5 1/K | - |
| - | 20.0 °C | Coefficient of thermal expansion of 1.15E-5 1/K | - |
| - | 100.0 °C | Coefficient of thermal expansion of 1.21E-5 1/K | - |
| - | 200.0 °C | Coefficient of thermal expansion of 1.27E-5 1/K | - |
| - | 300.0 °C | Coefficient of thermal expansion of 1.32E-5 1/K | - |
| - | 400.0 °C | Coefficient of thermal expansion of 1.36E-5 1/K | - |
| - | 500.0 °C | Coefficient of thermal expansion of 1.4E-5 1/K | - |
| - | 600.0 °C | Coefficient of thermal expansion of 1.44E-5 1/K | - |
| Max service temperature, long | - | Max service temperature, long of -60 - 0 °C | - |
| Melting point | - | Melting point of 1382 - 1529 °C | Typical for Chromium Molybdenum Steel |
| Specific heat capacity | -100.0 °C | Specific heat capacity of 423 J/(kg·K) | - |
| - | 20.0 °C | Specific heat capacity of 461 J/(kg·K) | - |
| - | 100.0 °C | Specific heat capacity of 479 J/(kg·K) | - |
| - | 200.0 °C | Specific heat capacity of 499 J/(kg·K) | - |
| - | 300.0 °C | Specific heat capacity of 517 J/(kg·K) | - |
| - | 400.0 °C | Specific heat capacity of 536 J/(kg·K) | - |
| - | 500.0 °C | Specific heat capacity of 558 J/(kg·K) | - |
| - | 600.0 °C | Specific heat capacity of 587 J/(kg·K) | - |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 41 W/(m·K) | - |
| - | 100.0 °C | Thermal conductivity of 42.7 W/(m·K) | - |
| - | 200.0 °C | Thermal conductivity of 42.8 W/(m·K) | - |
| - | 300.0 °C | Thermal conductivity of 41.6 W/(m·K) | - |
| - | 400.0 °C | Thermal conductivity of 39.9 W/(m·K) | - |
| - | 500.0 °C | Thermal conductivity of 37.8 W/(m·K) | - |
| - | 600.0 °C | Thermal conductivity of 35.6 W/(m·K) | - |
| Thermal diffusivity | 20.0 °C | Thermal diffusivity of 11.4 mm²/s | - |
| - | 100.0 °C | Thermal diffusivity of 11 mm²/s | - |
| - | 200.0 °C | Thermal diffusivity of 10.3 mm²/s | - |
| - | 300.0 °C | Thermal diffusivity of 9.5 mm²/s | - |
| - | 400.0 °C | Thermal diffusivity of 8.5 mm²/s | - |
| - | 500.0 °C | Thermal diffusivity of 7.3 mm²/s | - |
| - | 600.0 °C | Thermal diffusivity of 6 mm²/s | - |
DIN 1652-3 Grade 22CrMoS3-5 cold drawn or turned and soft annealed chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.19 - 0.24 % |
| Chromium | Chromium of 0.7 - 1 % |
| Manganese | Manganese of 0.7 - 1 % |
| Molybdenum | Molybdenum of 0.4 - 0.5 % |
| Phosphorus | Phosphorus of 0.04 % |
| Silicon | Silicon of 0.4 % |
| Sulfur | Sulfur of 0.02 - 0.035 % |
DIN 1652-3 Grade 22CrMoS3-5 cold drawn or turned and soft annealed electrical
| Property | Temperature | Value |
|---|---|---|
| Electrical resistivity | 20.0 °C | Electrical resistivity of 2.54E-7 Ω·m |
| - | 100.0 °C | Electrical resistivity of 3E-7 Ω·m |
| - | 200.0 °C | Electrical resistivity of 3.69E-7 Ω·m |
| - | 300.0 °C | Electrical resistivity of 4.51E-7 Ω·m |
| - | 400.0 °C | Electrical resistivity of 5.45E-7 Ω·m |
| - | 500.0 °C | Electrical resistivity of 6.54E-7 Ω·m |
| - | 600.0 °C | Electrical resistivity of 7.78E-7 Ω·m |
DIN 1652-3 Grade 22CrMoS3-5 cold drawn or turned and soft annealed mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | -100.0 °C | Elastic modulus of 217 GPa | - |
| - | 20.0 °C | Elastic modulus of 212 GPa | - |
| - | 100.0 °C | Elastic modulus of 207 GPa | - |
| - | 200.0 °C | Elastic modulus of 199 GPa | - |
| - | 300.0 °C | Elastic modulus of 192 GPa | - |
| - | 400.0 °C | Elastic modulus of 184 GPa | - |
| - | 500.0 °C | Elastic modulus of 175 GPa | - |
| - | 600.0 °C | Elastic modulus of 164 GPa | - |
| Hardness, Brinell | 20.0 °C | Hardness, Brinell of 217 [-] | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.29 [-] | Typical for Chromium Molybdenum Steel |
Experience a new standard of excellence as we redefine the benchmark in the steel industry, delivering unmatched quality and service.
-- Our promise
Similar or equivalent steel materials
- DIN 1652-3 Grade 20MoCrS4 treated to ferritic-pearlite structure and cold-drawn
- DIN 1652-3 Grade 20MoCrS4 cold drawn
- DIN 1652-3 Grade 20MoCrS4 cold-drawn or peeled and treated to ferrite-pearlite structure
- DIN 1652-3 Grade 20MoCrS4 cold drawn or turned and soft annealed
- DIN 1652-3 Grade 22CrMoS3-5 treated to ferritic-pearlite structure and cold-drawn
- DIN 1652-3 Grade 22CrMoS3-5 cold drawn
- DIN 1652-3 Grade 22CrMoS3-5 cold-drawn or peeled and treated to ferrite-pearlite structure
- DIN 17210 Grade 22CrMoS3-5 treated for cold shearing (+S)
- DIN 17210 Grade 20MoCrS4 soft annealed (+A)
- EN 10084 Grade 22CrMoS3-5 quenched (+Q)