DIN 1651 Grade 35SPb20 cold drawn and stress relieved
DIN 1651 Grade 35SPb20 cold drawn and stress relieved introduction
The fully killed machining steel 35 SPb 20 is used for mass parts of mean strength, especially for lower toughness demands cross-sectional. Its better machinable because of the Pb addition.
Application in the automotive engineering, toolbuilding, apparatus engineering (screws, nuts, smal parts).
Equivalent material: DIN 1.0756, AFNOR 35SPb20, BS 35SPb20, EN 35SPb20, EN 1.0756, ISO 35SPb20
DIN 1651 Grade 35SPb20 cold drawn and stress relieved general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
DIN 1651 Grade 35SPb20 cold drawn and stress relieved thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.1E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.18E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1380 - 1514 °C |
Typical for Medium Carbon Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 420 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 490 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 530 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 610 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 49 W/(m·K) |
- |
DIN 1651 Grade 35SPb20 cold drawn and stress relieved chemical
| Property |
Value |
| Carbon |
Carbon of 0.32 - 0.39 % |
| Lead |
Lead of 0.15 - 0.35 % |
| Manganese |
Manganese of 0.7 - 1.1 % |
| Phosphorus |
Phosphorus of 0.06 % |
| Silicon |
Silicon of 0.1 - 0.3 % |
| Sulfur |
Sulfur of 0.18 - 0.25 % |
DIN 1651 Grade 35SPb20 cold drawn and stress relieved electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.2E-7 Ω·m |
DIN 1651 Grade 35SPb20 cold drawn and stress relieved mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 210 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 193 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 185 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 175 GPa |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Medium Carbon Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 680 MPa |
- |
From concept to completion, we deliver excellence in every aspect of the steel supply chain.
-- Our promise
Similar or equivalent steel materials