ASTM A837 Grade 410
Equivalent material: DIN 1.4006, DIN X10Cr13, DIN X12Cr13, DIN GX10Cr13, AFNOR Z10C13, AFNOR Z13C13, AFNOR Z6C13, BS 410S21, UNI X12Cr13, SS 2302, UNE F.3401, AISI 410, SAE 410, JIS SUS410, JIS SUS410TKA, JIS SUS410TKC, EN X12Cr13, EN 1.4006, ISO X10Cr13, ISO C1, GOST 12Ch13, ASTM MT410, ASTM TP410, ASTM Grade CPCA15, UNS S41000, DIN 1.4024, DIN X15Cr13, AISI S41000, SAE S41000, JIS SUS410J1FB, JIS SUS410J1, JIS SUS410TB, JIS SUSF410B, JIS SUSF410C, JIS SUSF410A, JIS SUSF410D, EN X15Cr13, EN 1.4024, ISO X15Cr13, ASTM S41000
ASTM A837 Grade 410 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.7 g/cm³ |
Typical for Martensitic Stainless Steel |
ASTM A837 Grade 410 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K |
Typical for Martensitic Stainless Steel |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 460 J/(kg·K) |
Typical for Martensitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 31 W/(m·K) |
Typical for Martensitic Stainless Steel |
ASTM A837 Grade 410 chemical
| Property |
Value |
| Carbon |
Carbon of 0.15 % |
| Chromium |
Chromium of 11.5 - 13.5 % |
| Copper |
Copper of 0.35 % |
| Manganese |
Manganese of 1 % |
| Molybdenum |
Molybdenum of 0.1 % |
| Nickel |
Nickel of 0.5 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
ASTM A837 Grade 410 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
ASTM A837 Grade 410 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 229 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |