ASTM A815 Grade S41008 Heat-Treated
Equivalent material: DIN 1.4000, DIN X6Cr13, AFNOR Z8C13FF, AFNOR Z8C12, AFNOR X6Cr13, BS X6Cr13, BS 403S17, UNI X6Cr3, SS 2301, UNE F.3110, AISI 410S, AISI S41008, AISI 403, AISI S40300, SAE 410S, SAE S41008, SAE 403, SAE S40300, JIS SUS410S, JIS SUS403, JIS SUS403FB, EN X6Cr13, EN 1.4000, ISO 65, ISO X6Cr13, ISO 4000-410-08-I, ISO FP13G, GOST 08Ch13, GOST X6Cr13, GB/T 0Cr13, GB/T 06Cr13, GB/T S41008, ASTM MT403, ASTM 410S, UNS S41008, UNS S40300
ASTM A815 Grade S41008 Heat-Treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.7 g/cm³ |
Typical for Martensitic Stainless Steel |
ASTM A815 Grade S41008 Heat-Treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K |
Typical for Martensitic Stainless Steel |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 460 J/(kg·K) |
Typical for Martensitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 31 W/(m·K) |
Typical for Martensitic Stainless Steel |
ASTM A815 Grade S41008 Heat-Treated chemical
| Property |
Value |
| Carbon |
Carbon of 0.03 % |
| Chromium |
Chromium of 26 - 29 % |
| Manganese |
Manganese of 2 % |
| Molybdenum |
Molybdenum of 1 - 2.5 % |
| Nickel |
Nickel of 3.5 - 5.2 % |
| Nitrogen |
Nitrogen of 0.15 - 0.35 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.6 % |
| Sulfur |
Sulfur of 0.01 % |
ASTM A815 Grade S41008 Heat-Treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
ASTM A815 Grade S41008 Heat-Treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 22 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 183 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 415 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 205 MPa |
- |