ASTM A765 Grade I Normalized and Tempered, Double Normalized and Tempered, or Quenched and Tempered
Equivalent material: ASTM Grade I, UNS K02010
ASTM A765 Grade I Normalized and Tempered, Double Normalized and Tempered, or Quenched and Tempered general
Property |
Temperature |
Value |
Comment |
Density |
20.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
ASTM A765 Grade I Normalized and Tempered, Double Normalized and Tempered, or Quenched and Tempered thermal
Property |
Temperature |
Value |
Comment |
Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
ASTM A765 Grade I Normalized and Tempered, Double Normalized and Tempered, or Quenched and Tempered chemical
Property |
Value |
Aluminium |
Aluminium of 0.05 % |
Carbon |
Carbon of 0.3 % |
Chromium |
Chromium of 0.4 % |
Copper |
Copper of 0.35 % |
Manganese |
Manganese of 0.6 - 1.35 % |
Molybdenum |
Molybdenum of 0.1 % |
Nickel |
Nickel of 0.5 % |
Phosphorus |
Phosphorus of 0.02 % |
Silicon |
Silicon of 0.15 - 0.35 % |
Sulfur |
Sulfur of 0.02 % |
Vanadium |
Vanadium of 0.05 % |
ASTM A765 Grade I Normalized and Tempered, Double Normalized and Tempered, or Quenched and Tempered magnetic
Property |
Temperature |
Value |
Comment |
Curie temperature |
20.0 °C |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
ASTM A765 Grade I Normalized and Tempered, Double Normalized and Tempered, or Quenched and Tempered electrical
Property |
Temperature |
Value |
Comment |
Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ASTM A765 Grade I Normalized and Tempered, Double Normalized and Tempered, or Quenched and Tempered mechanical
Property |
Temperature |
Value |
Comment |
Charpy impact energy |
20.0 °C |
Charpy impact energy of 18 J |
- |
Elastic modulus |
20.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
Elongation A50 |
20.0 °C |
Elongation A50 of 25 % |
- |
Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
Reduction of area |
20.0 °C |
Reduction of area of 38 % |
- |
Shear modulus |
20.0 °C |
Shear modulus of 75 - 80 GPa |
Typical for Carbon Steel |
Tensile strength |
20.0 °C |
Tensile strength of 415 - 585 MPa |
- |
Yield Strength Rp0.2, short transverse |
20.0 °C |
Yield Strength Rp0.2, short transverse of 205 MPa |
- |
Trust our premium-grade steel products to deliver unmatched performance and durability for your projects.