ASTM A705 Grade S45503 Age-Hardening H1000
Equivalent material: UNS S45503
ASTM A705 Grade S45503 Age-Hardening H1000 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
Typical for Steel |
ASTM A705 Grade S45503 Age-Hardening H1000 chemical
| Property |
Value |
| Carbon |
Carbon of 0.01 % |
| Chromium |
Chromium of 11 - 12.5 % |
| Copper |
Copper of 1.5 - 2.5 % |
| Manganese |
Manganese of 0.5 % |
| Molybdenum |
Molybdenum of 0.5 % |
| Nickel |
Nickel of 7.5 - 9.5 % |
| Phosphorus |
Phosphorus of 0.01 % |
| Silicon |
Silicon of 0.2 % |
| Sulfur |
Sulfur of 0.01 % |
| Titanium |
Titanium of 1 - 1.35 % |
ASTM A705 Grade S45503 Age-Hardening H1000 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 190 - 210 GPa |
Typical for Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 6 - 10 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 363 [-] |
- |
| Hardness, Rockwell C |
23.0 °C |
Hardness, Rockwell C of 40 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 25 - 40 % |
- |
| Tensile strength |
23.0 °C |
Tensile strength of 1410 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 1280 MPa |
- |
Trust our expertise to deliver precision-engineered steel solutions for your specific needs.