ASTM A564 Grade S45503 H900
Equivalent material: UNS S45503
ASTM A564 Grade S45503 H900 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
Typical for Steel |
ASTM A564 Grade S45503 H900 chemical
| Property |
Value |
| Carbon |
Carbon of 0.05 % |
| Chromium |
Chromium of 14 - 16 % |
| Copper |
Copper of 1.25 - 1.75 % |
| Manganese |
Manganese of 1 % |
| Molybdenum |
Molybdenum of 0.5 - 1 % |
| Nickel |
Nickel of 5 - 7 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
ASTM A564 Grade S45503 H900 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 190 - 210 GPa |
Typical for Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 8 % |
- |
| Elongation A50, transverse |
23.0 °C |
Elongation A50, transverse of 4 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 444 [-] |
- |
| Hardness, Brinell, trans |
23.0 °C |
Hardness, Brinell, trans of 444 [-] |
- |
| Hardness, Rockwell C |
23.0 °C |
Hardness, Rockwell C of 47 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 30 % |
- |
| Reduction of area, transverse |
23.0 °C |
Reduction of area, transverse of 15 % |
- |
| Tensile strength |
23.0 °C |
Tensile strength of 1620 MPa |
- |
| Tensile strength, transverse |
23.0 °C |
Tensile strength, transverse of 1620 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 1520 MPa |
- |
| Yield strength Rp0.2, transverse |
23.0 °C |
Yield strength Rp0.2, transverse of 1520 MPa |
- |