ASTM A668 Class F Quenched and tempered, or normalized, quenched and tempered
Equivalent material: ASTM Class F, ASTM F, UNS K14048
ASTM A668 Class F Quenched and tempered, or normalized, quenched and tempered general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Chromium Molybdenum Steel |
ASTM A668 Class F Quenched and tempered, or normalized, quenched and tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.1E-5 - 1.4E-5 1/K |
Typical for Chromium Molybdenum Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Molybdenum Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 448 - 502 J/(kg·K) |
Typical for Chromium Molybdenum Steel |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 36 - 43 W/(m·K) |
Typical for Chromium Molybdenum Steel |
ASTM A668 Class F Quenched and tempered, or normalized, quenched and tempered electrical
| Property |
Value |
| Manganese |
Manganese of 1.35 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Sulfur |
Sulfur of 0.025 % |
ASTM A668 Class F Quenched and tempered, or normalized, quenched and tempered mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Chromium Molybdenum Steel |
| Elongation A50 |
20.0 °C |
Elongation A50 of 19 - 20 % |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 174 - 235 [-] |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Molybdenum Steel |
| Reduction of area |
20.0 °C |
Reduction of area of 36 - 39 % |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 565 - 620 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 330 - 380 MPa |
- |