ASTM A608 Grade HK30 As-Cast or As-Cast with Machining
Equivalent material: DIN 1.4848, DIN GX40CrNiSi25-20, AFNOR Z40CN2520, BS 310C40, BS 310C45, JIS SCH21, JIS SCH22, EN GX40CrNiSi25-20, EN 1.4848, ASTM Grade HK, UNS J94203, ASTM HK30
ASTM A608 Grade HK30 As-Cast or As-Cast with Machining general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
ASTM A608 Grade HK30 As-Cast or As-Cast with Machining thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
ASTM A608 Grade HK30 As-Cast or As-Cast with Machining chemical
| Property |
Value |
| Carbon |
Carbon of 0.25 - 0.35 % |
| Chromium |
Chromium of 23 - 27 % |
| Manganese |
Manganese of 1.5 % |
| Molybdenum |
Molybdenum of 0.5 % |
| Nickel |
Nickel of 19 - 22 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.5 - 2 % |
| Sulfur |
Sulfur of 0.04 % |
ASTM A608 Grade HK30 As-Cast or As-Cast with Machining electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
ASTM A608 Grade HK30 As-Cast or As-Cast with Machining mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation |
23.0 °C |
Elongation of 7 - 24 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 25 - 180 MPa |
- |
Experience the innovative edge of our steel solutions, designed to meet evolving industry needs.