ASTM A580 Grade 314 Condition A; Cold finished
Equivalent material: DIN 1.4841, DIN X15CrNiSi25-20, DIN X15CrNiSi25-21, AISI 314, SAE 314, JIS SUH310, JIS SUS310TP, JIS SUS310TB, JIS SUS310TF, EN X15CrNiSi25-21, EN 1.4841, GOST 20Ch25N20S2, GB 1Cr25Ni20Si2, UNS S31400, IS X20Cr2Ni20
ASTM A580 Grade 314 Condition A; Cold finished general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
ASTM A580 Grade 314 Condition A; Cold finished thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
ASTM A580 Grade 314 Condition A; Cold finished chemical
| Property |
Value |
| Carbon |
Carbon of 0.25 % |
| Chromium |
Chromium of 23 - 26 % |
| Manganese |
Manganese of 2 % |
| Nickel |
Nickel of 19 - 22 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1.5 - 3 % |
| Sulfur |
Sulfur of 0.03 % |
ASTM A580 Grade 314 Condition A; Cold finished electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
ASTM A580 Grade 314 Condition A; Cold finished mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 15 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 50 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 620 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 310 MPa |
- |