ASTM A542 Type B Class 1 Quenched and Tempered
  • Home
  • Material
  • ASTM A542 Type B Class 1 Quenched and Tempered

ASTM A542 Type B Class 1 Quenched and Tempered

Equivalent material: DIN 1.7703, DIN 13CrMoV9-10, BS 13CrMoV9-10, JIS SFVCMF22V, EN 13CrMoV9-10, EN 1.7703, ISO 13CrMoV9-10, ISO 14CrMoV9-10, ASTM Type D Class 1

ASTM A542 Type B Class 1 Quenched and Tempered general

Property Value Comment
Density Density of 7.8 - 7.9 g/cm³ Typical for Chromium Molybdenum Steel

ASTM A542 Type B Class 1 Quenched and Tempered thermal

Property Value Comment
Coefficient of thermal expansion Coefficient of thermal expansion of 1.1e-05 - 1.4e-05 1/K Typical for Chromium Molybdenum Steel
Melting point Melting point of 1382 - 1529 °C Typical for Chromium Molybdenum Steel
Specific heat capacity Specific heat capacity of 448 - 502 J/(kg·K) Typical for Chromium Molybdenum Steel
Thermal conductivity Thermal conductivity of 36 - 43 W/(m·K) Typical for Chromium Molybdenum Steel

ASTM A542 Type B Class 1 Quenched and Tempered chemical

Property Value Condition Related Standards Shape
Carbon Carbon of 0.11 - 0.15 % Quenched and Tempered ASTM A542 Plate
Chromium Chromium of 2 - 2.5 % Quenched and Tempered ASTM A542 Plate
Copper Copper of 0.25 % Quenched and Tempered ASTM A542 Plate
Manganese Manganese of 0.3 - 0.6 % Quenched and Tempered ASTM A542 Plate
Molybdenum Molybdenum of 0.9 - 1.1 % Quenched and Tempered ASTM A542 Plate
Nickel Nickel of 0.25 % Quenched and Tempered ASTM A542 Plate
Phosphorus Phosphorus of 0.015 % Quenched and Tempered ASTM A542 Plate
Silicon Silicon of 0.5 % Quenched and Tempered ASTM A542 Plate
Sulfur Sulfur of 0.015 % Quenched and Tempered ASTM A542 Plate
Vanadium Vanadium of 0.02 % Quenched and Tempered ASTM A542 Plate

ASTM A542 Type B Class 1 Quenched and Tempered electrical

Property Value Comment
Electrical conductivity Electrical conductivity of 3 S/m Predicted Value
Electrical resistivity Electrical resistivity of 36 Ω·m Predicted Value

ASTM A542 Type B Class 1 Quenched and Tempered mechanical

Property Value Condition Related Standards Shape Comment
Elastic modulus Elastic modulus of 200 - 215 GPa - - - Typical for Chromium Molybdenum Steel
Elongation Elongation of 11.9 % - - - Predicted Value, A200
- Elongation of 14 % Quenched and Tempered ASTM A542 Plate A50
- Elongation of 16.3 % - - - Predicted Value, A80
- Elongation of 18.1 % - - - Predicted Value, Transverse
- Elongation of 19.8 % - - - Predicted Value
- Elongation of 20.2 % - - - Predicted Value, A80 Transverse
Poisson's ratio Poisson's ratio of 0.29 [-] - - - Typical for Chromium Molybdenum Steel
Reduction of area Reduction of area of 43.0 % - - - Predicted Value
- Reduction of area of 45.0 % - - - Predicted Value, Transverse
Shear modulus Shear modulus of 79.7 GPa - - - Predicted Value
Shear strength Shear strength of 674.3 MPa - - - Predicted Value
Tensile strength Tensile strength of 725 - 860 MPa Quenched and Tempered ASTM A542 Plate -
Yield strength Yield strength of 301.2 MPa - - - Predicted Value, RP1
- Yield strength of 329.7 MPa - - - Predicted Value, RP1 Transverse
- Yield strength of 364.2 MPa - - - Predicted Value, RP05
- Yield strength of 496.6 MPa - - - Predicted Value, Transverse
- Yield strength of 500.9 MPa - - - Predicted Value, RP02 Transverse
- Yield strength of 585 MPa Quenched and Tempered ASTM A542 Plate -
- Yield strength of 602.3 MPa - - - Predicted Value, RP02
- Yield strength of 660.5 MPa - - - Predicted Value, RP002