ASTM A541 Grade 3V Quenched and Tempered
Equivalent material: DIN 1.7767, DIN 12CrMoV12-10, DIN 20CrMoVTiB4-10, BS 12CrMoV12-10, JIS SCMQV5, JIS SFVCMF3V, JIS SCMV5, JIS SCMQ5V, EN 12CrMoV12-10, EN 20CrMoVTiB4-10, EN 1.7767, ISO 12CrMoV12-10, ISO 13CrMoV12-10, ISO 14CrMoV9-10, ASTM Type D Class 1, ASTM Type E Class 4, ASTM Grade F3VCb, ASTM F3V
ASTM A541 Grade 3V Quenched and Tempered general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Chromium Molybdenum Steel |
ASTM A541 Grade 3V Quenched and Tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.1E-5 - 1.4E-5 1/K |
Typical for Chromium Molybdenum Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Molybdenum Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 448 - 502 J/(kg·K) |
Typical for Chromium Molybdenum Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 - 43 W/(m·K) |
Typical for Chromium Molybdenum Steel |
ASTM A541 Grade 3V Quenched and Tempered chemical
| Property |
Value |
| Boron |
Boron of 1E-3 - 3E-3 % |
| Carbon |
Carbon of 0.1 - 0.15 % |
| Chromium |
Chromium of 2.8 - 3.3 % |
| Manganese |
Manganese of 0.3 - 0.6 % |
| Molybdenum |
Molybdenum of 0.9 - 1.1 % |
| Phosphorus |
Phosphorus of 0.02 % |
| Silicon |
Silicon of 0.1 % |
| Sulfur |
Sulfur of 0.02 % |
| Titanium |
Titanium of 0.02 - 0.04 % |
| Vanadium |
Vanadium of 0.2 - 0.3 % |
ASTM A541 Grade 3V Quenched and Tempered mechanical
| Property |
Temperature |
Value |
Comment |
| Charpy impact energy |
23.0 °C |
Charpy impact energy of 54 J |
- |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Chromium Molybdenum Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 18 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Molybdenum Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 45 % |
- |
| Tensile strength |
23.0 °C |
Tensile strength of 585 - 760 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 415 MPa |
- |