ASTM A517 Grade F Quenched and Tempered

ASTM A517 Grade F Quenched and Tempered

Equivalent material: DIN 1.0529, DIN StE 350-3Z, DIN FeE350G, DIN StE 350-3 Z, DIN S350GD, AFNOR S350GD, BS S350GD, JIS SGC490, JIS SGMC440, JIS SZAC490, JIS SZAH490, JIS SGLC490, JIS SGLH490, EN S350GD, EN 1.0529, ISO 350, GOST 350, GB/T S350GD, ASTM HSLAS Grade 340 Class 1

ASTM A517 Grade F Quenched and Tempered general

Property Value Comment
Density Density of 7.8 - 7.9 g/cm³ Typical for Low Carbon Steel

ASTM A517 Grade F Quenched and Tempered thermal

Property Value Comment
Coefficient of thermal expansion Coefficient of thermal expansion of 1.32e-05 - 1.38e-05 1/K Typical for Low Carbon Steel
Max service temperature Max service temperature of 361.5 °C Predicted Value, Long
- Max service temperature of 500 °C Typical for Carbon Steel
Melting point Melting point of 1480 - 1526 °C Typical for Low Carbon Steel
Specific heat capacity Specific heat capacity of 465 J/(kg·K) Typical for Low Carbon Steel
Thermal conductivity Thermal conductivity of 25 - 93 W/(m·K) Typical for Low Carbon Steel

ASTM A517 Grade F Quenched and Tempered chemical

Property Value Condition Related Standards Shape
Boron Boron of 0.0005 - 0.006 % Quenched and Tempered ASTM A517 Plate
Carbon Carbon of 0.1 - 0.2 % Quenched and Tempered ASTM A517 Plate
Chromium Chromium of 0.4 - 0.65 % Quenched and Tempered ASTM A517 Plate
Copper Copper of 0.15 - 0.5 % Quenched and Tempered ASTM A517 Plate
Manganese Manganese of 0.6 - 1 % Quenched and Tempered ASTM A517 Plate
Molybdenum Molybdenum of 0.4 - 0.6 % Quenched and Tempered ASTM A517 Plate
Nickel Nickel of 0.7 - 1 % Quenched and Tempered ASTM A517 Plate
Phosphorus Phosphorus of 0.025 % Quenched and Tempered ASTM A517 Plate
Silicon Silicon of 0.15 - 0.35 % Quenched and Tempered ASTM A517 Plate
Sulfur Sulfur of 0.025 % Quenched and Tempered ASTM A517 Plate
Titanium Titanium of 0.1 % Quenched and Tempered ASTM A517 Plate
Vanadium Vanadium of 0.03 - 0.08 % Quenched and Tempered ASTM A517 Plate

ASTM A517 Grade F Quenched and Tempered magnetic

Property Value Comment
Curie temperature Curie temperature of 770 °C Typical for Low Carbon Steel

ASTM A517 Grade F Quenched and Tempered electrical

Property Value Comment
Electrical conductivity Electrical conductivity of 3 S/m Predicted Value
Electrical resistivity Electrical resistivity of 1.43e-07 - 1.74e-07 Ω·m Typical for Carbon Steel

ASTM A517 Grade F Quenched and Tempered mechanical

Property Value Condition Related Standards Shape Comment
Elastic modulus Elastic modulus of 200 - 215 GPa - - - Typical for Low Carbon Steel
Elongation Elongation of 12.6 % - - - Predicted Value, A200
- Elongation of 14 % Quenched and Tempered ASTM A517 Plate A50
- Elongation of 14.4 % - - - Predicted Value, A80
- Elongation of 16 % Quenched and Tempered ASTM A517 Plate A50
- Elongation of 18.1 % - - - Predicted Value, Transverse
- Elongation of 19.1 % - - - Predicted Value
- Elongation of 19.4 % - - - Predicted Value, A80 Transverse
Poisson's ratio Poisson's ratio of 0.29 [-] - - - Typical for Low Carbon Steel
Reduction of area Reduction of area of 42.5 % - - - Predicted Value, Transverse
- Reduction of area of 45 % Quenched and Tempered ASTM A517 Plate -
Shear modulus Shear modulus of 82 GPa - - - Typical for Low Carbon Steel
Shear strength Shear strength of 646.7 MPa - - - Predicted Value
Tensile strength Tensile strength of 725 - 930 MPa Quenched and Tempered ASTM A517 Plate -
- Tensile strength of 795 - 930 MPa Quenched and Tempered ASTM A517 Plate -
Yield strength Yield strength of 315.5 MPa - - - Predicted Value, RP1
- Yield strength of 328.3 MPa - - - Predicted Value, RP1 Transverse
- Yield strength of 405 MPa - - - Predicted Value, RP05
- Yield strength of 467.9 MPa - - - Predicted Value, RP02 Transverse
- Yield strength of 497.1 MPa - - - Predicted Value, Transverse
- Yield strength of 606.1 MPa - - - Predicted Value, RP02
- Yield strength of 620 MPa Quenched and Tempered ASTM A517 Plate -
- Yield strength of 690 MPa Quenched and Tempered ASTM A517 Plate -
- Yield strength of 740.1 MPa - - - Predicted Value, RP002