ASTM A203 Grade F Quenched and Tempered

ASTM A203 Grade F Quenched and Tempered

Equivalent material: DIN 1.0529, EN 1.0529, DIN StE 350-3Z, DIN FeE350G, DIN StE 350-3 Z, DIN S350GD, AFNOR S350GD, BS S350GD, JIS SGC490, JIS SGMC440, JIS SZAC490, JIS SZAH490, JIS SGLC490, JIS SGLH490, EN S350GD, ISO 350, GOST 350, GB/T S350GD, ASTM HSLAS Grade 340 Class 1

ASTM A203 Grade F Quenched and Tempered general

Property Value Comment
Density Density of 7.8 - 7.9 g/cm³ Typical for Low Carbon Steel

ASTM A203 Grade F Quenched and Tempered thermal

Property Value Comment
Coefficient of thermal expansion Coefficient of thermal expansion of 1.32e-05 - 1.38e-05 1/K Typical for Low Carbon Steel
Max service temperature Max service temperature of 337.4 °C Predicted Value, Long
- Max service temperature of 500 °C Typical for Carbon Steel
Melting point Melting point of 1480 - 1526 °C Typical for Low Carbon Steel
Specific heat capacity Specific heat capacity of 465 J/(kg·K) Typical for Low Carbon Steel
Thermal conductivity Thermal conductivity of 25 - 93 W/(m·K) Typical for Low Carbon Steel

ASTM A203 Grade F Quenched and Tempered chemical

Property Value Condition Related Standards Shape
Carbon Carbon of 0.2 % Quenched and Tempered ASTM A203 Plate
Manganese Manganese of 0.7 % Quenched and Tempered ASTM A203 Plate
Nickel Nickel of 3.25 - 3.75 % Quenched and Tempered ASTM A203 Plate
Phosphorus Phosphorus of 0.7 % Quenched and Tempered ASTM A203 Plate
Silicon Silicon of 0.15 - 0.4 % Quenched and Tempered ASTM A203 Plate
Sulfur Sulfur of 0.8 % Quenched and Tempered ASTM A203 Plate

ASTM A203 Grade F Quenched and Tempered magnetic

Property Value Comment
Curie temperature Curie temperature of 770 °C Typical for Low Carbon Steel

ASTM A203 Grade F Quenched and Tempered electrical

Property Value Comment
Electrical conductivity Electrical conductivity of 7 S/m Predicted Value
Electrical resistivity Electrical resistivity of 1.43e-07 - 1.74e-07 Ω·m Typical for Carbon Steel

ASTM A203 Grade F Quenched and Tempered mechanical

Property Value Condition Related Standards Shape Comment
Elastic modulus Elastic modulus of 200 - 215 GPa - - - Typical for Low Carbon Steel
Elongation Elongation of 16.7 % - - - Predicted Value, A200
- Elongation of 19.0 % - - - Predicted Value, Transverse
- Elongation of 19.5 % - - - Predicted Value, A80
- Elongation of 20 % Quenched and Tempered ASTM A203 Plate A50
- Elongation of 20.8 % - - - Predicted Value, A80 Transverse
- Elongation of 21.8 % - - - Predicted Value
Hardness, Brinell Hardness, Brinell of 262 [-] - - - Predicted Value, Transverse
Poisson's ratio Poisson's ratio of 0.29 [-] - - - Typical for Low Carbon Steel
Reduction of area Reduction of area of 43.1 % - - - Predicted Value
- Reduction of area of 43.6 % - - - Predicted Value, Transverse
Shear modulus Shear modulus of 82 GPa - - - Typical for Low Carbon Steel
Shear strength Shear strength of 526 MPa - - - Predicted Value
Tensile strength Tensile strength of 550 - 690 MPa Quenched and Tempered ASTM A203 Plate -
Yield strength Yield strength of 263.2 MPa - - - Predicted Value, RP1
- Yield strength of 297.6 MPa - - - Predicted Value, RP05
- Yield strength of 317.5 MPa - - - Predicted Value, RP1 Transverse
- Yield strength of 343.2 MPa - - - Predicted Value, Transverse
- Yield strength of 345 MPa Quenched and Tempered ASTM A203 Plate -
- Yield strength of 380 MPa Quenched and Tempered ASTM A203 Plate -
- Yield strength of 414.1 MPa - - - Predicted Value, RP02
- Yield strength of 473.4 MPa - - - Predicted Value, RP002
- Yield strength of 475.8 MPa - - - Predicted Value, RP02 Transverse

Trust our high-quality steel to forge a brighter and stronger future for your projects.

-- Our promise