ASTM A311 Grade 1035 Normal Draft Cold Drawn and Stress Relief Annealed
Equivalent material: DIN 1.0516, DIN D 35-2, DIN C38D, AFNOR C38D, BS C38D, AISI 1035, SAE 1035, JIS SWRH37, JIS CS40, JIS 50H, EN C38D, EN 1.0516, ISO C38D, GB/T C38D, GB/T U53382, UNS G10350
ASTM A311 Grade 1035 Normal Draft Cold Drawn and Stress Relief Annealed general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Medium Carbon Steel |
ASTM A311 Grade 1035 Normal Draft Cold Drawn and Stress Relief Annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
Typical for Medium Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1380 - 1514 °C |
Typical for Medium Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 470 - 520 J/(kg·K) |
Typical for Medium Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 21 - 52 W/(m·K) |
Typical for Medium Carbon Steel |
ASTM A311 Grade 1035 Normal Draft Cold Drawn and Stress Relief Annealed chemical
| Property |
Value |
| Carbon |
Carbon of 0.32 - 0.38 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Sulfur |
Sulfur of 0.05 % |
ASTM A311 Grade 1035 Normal Draft Cold Drawn and Stress Relief Annealed electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ASTM A311 Grade 1035 Normal Draft Cold Drawn and Stress Relief Annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Medium Carbon Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 10 - 13 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Medium Carbon Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 30 - 35 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 75 - 80 GPa |
Typical for Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 485 - 590 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 415 - 520 MPa |
- |