ASTM A249 Grade TP304 Heat-Treated
Equivalent material: AISI 304, SAE 304, JIS SUS304, UNS S30400, DIN 1.4301, DIN X 5 CrNi 18 9, DIN X5CrNi18-10, AFNOR Z6CN18-09, AFNOR Z7CN18-09, BS 304S15, BS 304S31, UNI X5CrNi1810, SS 2332, UNE F.3551, JIS SUS304TBS, JIS SUS304TPD, JIS SUS304TP, JIS SUS304TPY, JIS SUS304TB, JIS SUS304TF, JIS SUS304TKA, JIS SUS304TKC, JIS SUSF304, EN X5CrNi18-10, EN 1.4301, ISO A2, GOST 08Ch18N10, GB 0Cr18Ni9, ASTM Grade B8, ASTM Grade B8A, ASTM 304
ASTM A249 Grade TP304 Heat-Treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
ASTM A249 Grade TP304 Heat-Treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
ASTM A249 Grade TP304 Heat-Treated chemical
| Property |
Value |
| Carbon |
Carbon of 0.08 % |
| Chromium |
Chromium of 18 - 20 % |
| Manganese |
Manganese of 2 % |
| Nickel |
Nickel of 8 - 11 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
ASTM A249 Grade TP304 Heat-Treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
ASTM A249 Grade TP304 Heat-Treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 35 % |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 90 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 200 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 515 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 205 MPa |
- |