ASTM A213 Grade T2
Equivalent material: DIN 1.7332, DIN 17CrMo3-5, JIS SFVAF2, JIS STPA20, JIS STBA20, JIS SCMV1, EN 17CrMo3-5, EN 1.7332, DIN 1.7335, DIN 13CrMo4-4, DIN 13CrMo4-5, AFNOR 15CD3.5, AFNOR 15CD4.5, BS 1501-620-Gr27, BS 13CrMo4-5, UNI 14CrMo45, UNE 14CrMo45, JIS SPVAF12, JIS STPA22, JIS STBA22, JIS SCMV2, JIS STFA22, JIS SFVAF12, EN 13CrMo4-5, EN 1.7335, ISO 13CrMo4-5, ISO 14CrMo4-5+NT1, ISO 14CrMo4-5+NT2, UNS K11562
ASTM A213 Grade T2 general
Property |
Temperature |
Value |
Comment |
Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Chromium Molybdenum Steel |
ASTM A213 Grade T2 thermal
Property |
Temperature |
Value |
Comment |
Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.1E-5 - 1.4E-5 1/K |
Typical for Chromium Molybdenum Steel |
Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Molybdenum Steel |
Specific heat capacity |
23.0 °C |
Specific heat capacity of 448 - 502 J/(kg·K) |
Typical for Chromium Molybdenum Steel |
Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 - 43 W/(m·K) |
Typical for Chromium Molybdenum Steel |
ASTM A213 Grade T2 chemical
Property |
Value |
Carbon |
Carbon of 0.1 - 0.2 % |
Chromium |
Chromium of 0.5 - 0.81 % |
Manganese |
Manganese of 0.3 - 0.61 % |
Molybdenum |
Molybdenum of 0.44 - 0.65 % |
Phosphorus |
Phosphorus of 0.03 % |
Silicon |
Silicon of 0.1 - 0.3 % |
Sulfur |
Sulfur of 0.025 % |
ASTM A213 Grade T2 mechanical
Property |
Temperature |
Value |
Comment |
Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Chromium Molybdenum Steel |
Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Molybdenum Steel |