EN 10028-2 Grade 13CrMo4-5 normalized and tempered (+NT)
EN 10028-2 Grade 13CrMo4-5 normalized and tempered (+NT) introduction
Heat-resistant steel for pressure purposes.
Application: tank construction, collectors, flanges and prewelded collars, in apparatus engineering and in petrochemical industry
Equivalent material: GB A30122, GB 12CrMo, IS 12Cr4Mo5H, IS SCMV2, GOST 12ChM, GOST 15ChM, KS SCMV2, ASTM A387 Grade 11, ASTM A387 Grade 12, UNS K11757, UNS K11789, DIN 13CrMo4-5, IS 13CrMo4-5, GOST 12ХM, GOST 15ХM, DIN 13CrMo4-4, NBN 14CrMo45, AFNOR 15CD3.5, AFNOR 15CD4.5, BS 470, BS 540, BS 620-440, IS P32, UNI 14CrMo3, UNI 16CrMo3, IS SFVAF12, ÖNORM 13CrMo4-4KW, PN 15HM, SS 2216, UNE F.2631-14CrMo4-5, ASTM Grade 12, DIN 1.7335, AFNOR 15CD3-5, AFNOR 15CD4-5, BS 1501-620-Gr27, BS 13CrMo4-5, UNI 14CrMo45, UNE 14CrMo45, JIS SPVAF12, JIS STPA22, JIS STBA22, JIS SCMV2, JIS STFA22, JIS STBA20, JIS SFVAF12, EN 1.7335, ISO 13CrMo4-5, ISO 14CrMo4-5+NT1, ISO 14CrMo4-5+NT2, ASTM Grade T2, UNS K11562
EN 10028-2 Grade 13CrMo4-5 normalized and tempered (+NT) general
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
| Density | 20 °C | Density of 7.848 - 7.85 g/cm³ | normalized and tempered (+NT) | EN 10028-2 | Flat |
| - | 20 °C | Density of 7.848 g/cm³ | normalized and tempered (+NT) | EN 10028-2 | Flat |
| - | 20 °C | Density of 7.85 g/cm³ | normalized and tempered (+NT) | EN 10028-2 | Flat |
| - | 50 °C | Density of 7.839 g/cm³ | normalized and tempered (+NT) | EN 10028-2 | Flat |
| - | 100 °C | Density of 7.824 g/cm³ | normalized and tempered (+NT) | EN 10028-2 | Flat |
| - | 150 °C | Density of 7.809 g/cm³ | normalized and tempered (+NT) | EN 10028-2 | Flat |
| - | 200 °C | Density of 7.792 g/cm³ | normalized and tempered (+NT) | EN 10028-2 | Flat |
| - | 250 °C | Density of 7.774 g/cm³ | normalized and tempered (+NT) | EN 10028-2 | Flat |
| - | 300 °C | Density of 7.756 g/cm³ | normalized and tempered (+NT) | EN 10028-2 | Flat |
| - | 350 °C | Density of 7.738 g/cm³ | normalized and tempered (+NT) | EN 10028-2 | Flat |
| - | 400 °C | Density of 7.719 g/cm³ | normalized and tempered (+NT) | EN 10028-2 | Flat |
| - | 450 °C | Density of 7.7 g/cm³ | normalized and tempered (+NT) | EN 10028-2 | Flat |
| - | 500 °C | Density of 7.681 g/cm³ | normalized and tempered (+NT) | EN 10028-2 | Flat |
| - | 550 °C | Density of 7.662 g/cm³ | normalized and tempered (+NT) | EN 10028-2 | Flat |
| - | 600 °C | Density of 7.643 g/cm³ | normalized and tempered (+NT) | EN 10028-2 | Flat |
EN 10028-2 Grade 13CrMo4-5 normalized and tempered (+NT) thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Coefficient of thermal expansion | -100 °C | Coefficient of thermal expansion of 1.05e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Coefficient of thermal expansion of 1.15e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Coefficient of thermal expansion of 1.21e-05 - 1.22e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Coefficient of thermal expansion of 1.21e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Coefficient of thermal expansion of 1.22e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Coefficient of thermal expansion of 1.27e-05 - 1.29e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Coefficient of thermal expansion of 1.27e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Coefficient of thermal expansion of 1.29e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Coefficient of thermal expansion of 1.32e-05 - 1.34e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Coefficient of thermal expansion of 1.32e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Coefficient of thermal expansion of 1.34e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Coefficient of thermal expansion of 1.36e-05 - 1.4e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Coefficient of thermal expansion of 1.36e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Coefficient of thermal expansion of 1.4e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Coefficient of thermal expansion of 1.4e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Coefficient of thermal expansion of 1.4e-05 - 1.43e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Coefficient of thermal expansion of 1.43e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Coefficient of thermal expansion of 1.44e-05 - 1.46e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Coefficient of thermal expansion of 1.44e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Coefficient of thermal expansion of 1.46e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| Max service temperature | - | Max service temperature of 400 - 550 °C | normalized and tempered (+NT) | EN 10028-2 | Flat | Long |
| Melting point | - | Melting point of 1382 - 1529 °C | - | - | - | Typical for Chromium Molybdenum Steel |
| Specific heat capacity | -100 °C | Specific heat capacity of 423 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Specific heat capacity of 430 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Specific heat capacity of 430 - 461 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Specific heat capacity of 461 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Specific heat capacity of 479 - 500 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Specific heat capacity of 479 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Specific heat capacity of 500 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Specific heat capacity of 499 - 540 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Specific heat capacity of 499 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Specific heat capacity of 540 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Specific heat capacity of 517 - 580 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Specific heat capacity of 517 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Specific heat capacity of 580 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Specific heat capacity of 536 - 620 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Specific heat capacity of 536 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Specific heat capacity of 620 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Specific heat capacity of 558 - 690 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Specific heat capacity of 558 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Specific heat capacity of 690 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Specific heat capacity of 587 - 780 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Specific heat capacity of 587 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Specific heat capacity of 780 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| Thermal conductivity | 20 °C | Thermal conductivity of 45.9 - 46 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Thermal conductivity of 45.9 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Thermal conductivity of 46 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Thermal conductivity of 46 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Thermal conductivity of 46 - 46.4 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Thermal conductivity of 46.4 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Thermal conductivity of 45.6 - 46 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Thermal conductivity of 45.6 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Thermal conductivity of 46 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Thermal conductivity of 43 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Thermal conductivity of 43 - 43.5 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Thermal conductivity of 43.5 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Thermal conductivity of 40.9 - 41 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Thermal conductivity of 40.9 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Thermal conductivity of 41 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Thermal conductivity of 38 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Thermal conductivity of 38 - 38.2 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Thermal conductivity of 38.2 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Thermal conductivity of 35.5 - 36 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Thermal conductivity of 35.5 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Thermal conductivity of 36 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| Thermal diffusivity | 20 °C | Thermal diffusivity of 12.7 mm²/s | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Thermal diffusivity of 12 mm²/s | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Thermal diffusivity of 11 mm²/s | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Thermal diffusivity of 9.9 mm²/s | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Thermal diffusivity of 8.7 mm²/s | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Thermal diffusivity of 7.3 mm²/s | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Thermal diffusivity of 6 mm²/s | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
EN 10028-2 Grade 13CrMo4-5 normalized and tempered (+NT) chemical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Carbon | Carbon of 0.08 - 0.18 % | normalized and tempered (+NT) | EN 10028-2 | Flat |
| Chromium | Chromium of 0.7 - 1.15 % | normalized and tempered (+NT) | EN 10028-2 | Flat |
| Copper | Copper of 0.3 % | normalized and tempered (+NT) | EN 10028-2 | Flat |
| Manganese | Manganese of 0.4 - 1 % | normalized and tempered (+NT) | EN 10028-2 | Flat |
| Molybdenum | Molybdenum of 0.4 - 0.6 % | normalized and tempered (+NT) | EN 10028-2 | Flat |
| Nitrogen | Nitrogen of 0.012 % | normalized and tempered (+NT) | EN 10028-2 | Flat |
| Phosphorus | Phosphorus of 0.025 % | normalized and tempered (+NT) | EN 10028-2 | Flat |
| Silicon | Silicon of 0.35 % | normalized and tempered (+NT) | EN 10028-2 | Flat |
| Sulfur | Sulfur of 0.01 % | normalized and tempered (+NT) | EN 10028-2 | Flat |
EN 10028-2 Grade 13CrMo4-5 normalized and tempered (+NT) electrical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Electrical conductivity | - | Electrical conductivity of 4 S/m | - | - | - | Predicted Value |
| Electrical resistivity | 20 °C | Electrical resistivity of 2.27e-07 - 2.3e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Electrical resistivity of 2.27e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Electrical resistivity of 2.27e-07 - 2.37e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Electrical resistivity of 2.3e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Electrical resistivity of 2.3e-07 - 2.37e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Electrical resistivity of 2.37e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 50 °C | Electrical resistivity of 2.56e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Electrical resistivity of 2.76e-07 - 2.8e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Electrical resistivity of 2.76e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Electrical resistivity of 2.76e-07 - 2.88e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Electrical resistivity of 2.8e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Electrical resistivity of 2.8e-07 - 2.88e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Electrical resistivity of 2.88e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 150 °C | Electrical resistivity of 3.21e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Electrical resistivity of 3.46e-07 - 3.5e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Electrical resistivity of 3.46e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Electrical resistivity of 3.46e-07 - 3.59e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Electrical resistivity of 3.5e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Electrical resistivity of 3.5e-07 - 3.59e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Electrical resistivity of 3.59e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 250 °C | Electrical resistivity of 4.01e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Electrical resistivity of 4.3e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Electrical resistivity of 4.3e-07 - 4.31e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Electrical resistivity of 4.3e-07 - 4.45e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Electrical resistivity of 4.31e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Electrical resistivity of 4.31e-07 - 4.45e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Electrical resistivity of 4.45e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 350 °C | Electrical resistivity of 4.95e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Electrical resistivity of 5.3e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Electrical resistivity of 5.3e-07 - 5.32e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Electrical resistivity of 5.3e-07 - 5.48e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Electrical resistivity of 5.32e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Electrical resistivity of 5.32e-07 - 5.48e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Electrical resistivity of 5.48e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 450 °C | Electrical resistivity of 6.06e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Electrical resistivity of 6.48e-07 - 6.5e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Electrical resistivity of 6.48e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Electrical resistivity of 6.48e-07 - 6.63e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Electrical resistivity of 6.5e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Electrical resistivity of 6.5e-07 - 6.63e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Electrical resistivity of 6.63e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 550 °C | Electrical resistivity of 7.28e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Electrical resistivity of 7.8e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Electrical resistivity of 7.8e-07 - 7.81e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Electrical resistivity of 7.8e-07 - 7.97e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Electrical resistivity of 7.81e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Electrical resistivity of 7.81e-07 - 7.97e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Electrical resistivity of 7.97e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
EN 10028-2 Grade 13CrMo4-5 normalized and tempered (+NT) mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Elastic modulus | -100 °C | Elastic modulus of 217 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Elastic modulus of 212 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Elastic modulus of 212 - 212.5 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Elastic modulus of 212.5 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 50 °C | Elastic modulus of 211.6 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Elastic modulus of 207 - 209 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Elastic modulus of 207 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Elastic modulus of 207 - 208.9 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Elastic modulus of 208.9 - 209 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Elastic modulus of 208.9 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Elastic modulus of 209 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 150 °C | Elastic modulus of 205.5 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Elastic modulus of 199 - 202 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Elastic modulus of 199 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Elastic modulus of 199 - 201.8 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Elastic modulus of 201.8 - 202 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Elastic modulus of 201.8 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Elastic modulus of 202 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 250 °C | Elastic modulus of 197.7 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Elastic modulus of 192 - 193 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Elastic modulus of 192 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Elastic modulus of 192 - 193.4 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Elastic modulus of 193 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Elastic modulus of 193 - 193.4 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Elastic modulus of 193.4 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 350 °C | Elastic modulus of 189.2 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Elastic modulus of 184 - 185 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Elastic modulus of 184 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Elastic modulus of 184 - 184.8 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Elastic modulus of 184.8 - 185 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Elastic modulus of 184.8 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Elastic modulus of 185 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 450 °C | Elastic modulus of 180.4 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Elastic modulus of 175 - 176 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Elastic modulus of 175 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Elastic modulus of 175 - 175.9 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Elastic modulus of 175.9 - 176 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Elastic modulus of 175.9 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Elastic modulus of 176 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 550 °C | Elastic modulus of 171.3 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Elastic modulus of 164 - 166 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Elastic modulus of 164 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Elastic modulus of 164 - 166.6 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Elastic modulus of 166 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Elastic modulus of 166 - 166.6 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Elastic modulus of 166.6 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| Elongation | - | Elongation of 16.5 % | - | - | - | Predicted Value, A80 Transverse |
| - | - | Elongation of 17.6 % | - | - | - | Predicted Value, A80 |
| - | - | Elongation of 18.0 % | - | - | - | Predicted Value, A200 |
| - | - | Elongation of 20.2 % | - | - | - | Predicted Value, A5 |
| - | - | Elongation of 22.1 % | - | - | - | Predicted Value, A50 |
| - | 20 °C | Elongation of 19 % | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Elongation of 19 % | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| Hardness, Brinell | - | Hardness, Brinell of 224 [-] | - | - | - | Predicted Value, Transverse |
| Poisson's ratio | 20 °C | Poisson's ratio of 0.283 [-] | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Poisson's ratio of 0.284 [-] | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 50 °C | Poisson's ratio of 0.284 [-] | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Poisson's ratio of 0.283 [-] | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 150 °C | Poisson's ratio of 0.285 [-] | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Poisson's ratio of 0.287 [-] | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 250 °C | Poisson's ratio of 0.29 [-] | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Poisson's ratio of 0.292 [-] | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 350 °C | Poisson's ratio of 0.295 [-] | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Poisson's ratio of 0.296 [-] | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 450 °C | Poisson's ratio of 0.299 [-] | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Poisson's ratio of 0.301 [-] | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 550 °C | Poisson's ratio of 0.305 [-] | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Poisson's ratio of 0.31 [-] | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| Reduction of area | - | Reduction of area of 43.4 % | - | - | - | Predicted Value |
| - | - | Reduction of area of 43.9 % | - | - | - | Predicted Value, Transverse |
| Shear modulus | 20 °C | Shear modulus of 82.8 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 50 °C | Shear modulus of 82.4 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Shear modulus of 81.4 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 150 °C | Shear modulus of 80.0 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Shear modulus of 78.4 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 250 °C | Shear modulus of 76.6 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Shear modulus of 74.8 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 350 °C | Shear modulus of 73.1 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Shear modulus of 71.3 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 450 °C | Shear modulus of 69.5 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Shear modulus of 67.6 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 550 °C | Shear modulus of 65.6 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Shear modulus of 63.6 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| Shear strength | - | Shear strength of 602.2 MPa | - | - | - | Predicted Value |
| Tensile strength | 20 °C | Tensile strength of 430 - 600 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Tensile strength of 430 - 590 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Tensile strength of 430 - 580 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Tensile strength of 430 - 600 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 430 - 590 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 430 - 580 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 440 - 600 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Tensile strength of 440 - 590 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Tensile strength of 440 - 580 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Tensile strength of 440 - 600 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 440 - 590 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 440 - 580 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 450 - 600 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Tensile strength of 450 - 590 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Tensile strength of 450 - 580 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Tensile strength of 450 - 600 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 450 - 590 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 450 - 580 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| Yield strength | - | Yield strength of 256 MPa | - | - | - | Predicted Value, RP1 |
| - | - | Yield strength of 265.2 MPa | - | - | - | Predicted Value, RP1 Transverse |
| - | - | Yield strength of 367.8 MPa | - | - | - | Predicted Value, RP05 |
| - | - | Yield strength of 368.9 MPa | - | - | - | Predicted Value, RP02 Transverse |
| - | - | Yield strength of 481.7 MPa | - | - | - | Predicted Value, RP002 |
| - | 20 °C | Yield strength of 255 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Yield strength of 255 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Yield strength of 270 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Yield strength of 270 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Yield strength of 290 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Yield strength of 290 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Yield strength of 300 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Yield strength of 300 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 50 °C | Yield strength of 250 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 50 °C | Yield strength of 265 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 50 °C | Yield strength of 285 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 50 °C | Yield strength of 294 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 100 °C | Yield strength of 242 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 100 °C | Yield strength of 256 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 100 °C | Yield strength of 275 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 100 °C | Yield strength of 285 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 150 °C | Yield strength of 229 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 150 °C | Yield strength of 242 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 150 °C | Yield strength of 260 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 150 °C | Yield strength of 269 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 200 °C | Yield strength of 214 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 200 °C | Yield strength of 227 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 200 °C | Yield strength of 243 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 200 °C | Yield strength of 252 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 250 °C | Yield strength of 199 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 250 °C | Yield strength of 210 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 250 °C | Yield strength of 226 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 250 °C | Yield strength of 234 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 300 °C | Yield strength of 184 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 300 °C | Yield strength of 195 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 300 °C | Yield strength of 209 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 300 °C | Yield strength of 216 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 350 °C | Yield strength of 170 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 350 °C | Yield strength of 180 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 350 °C | Yield strength of 194 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 350 °C | Yield strength of 200 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 400 °C | Yield strength of 159 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 400 °C | Yield strength of 168 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 400 °C | Yield strength of 180 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 400 °C | Yield strength of 186 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 450 °C | Yield strength of 148 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 450 °C | Yield strength of 157 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 450 °C | Yield strength of 169 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 450 °C | Yield strength of 175 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 500 °C | Yield strength of 139 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 500 °C | Yield strength of 148 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 500 °C | Yield strength of 159 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 500 °C | Yield strength of 164 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
Our rigorous quality control measures guarantee the reliability and consistency of our steel products.
-- Our promise
Similar or equivalent steel materials
- EN 10028-2 Grade 13CrMoSi5-5 quenched and tempered (+QT)
- EN 10028-2 Grade 13CrMo4-5 quenched and tempered (+QT)
- EN 10216-2 Grade 13CrMo4-5 normalized and tempered (+NT)
- EN 10222-2 Grade 13CrMo4-5 normalized and tempered (+NT)
- EN 10222-2 Grade 13CrMo4-5 quenched and tempered (+QT)
- EN 10273 Grade 13CrMo4-5 normalized and tempered (+NT)
- DIN 17155 Grade 13CrMo4-4 quenched and tempered (+QT)
- EN 10273 Grade 13CrMo4-5 normalized and tempered or quenched and tempered
- EN 10273 Grade 13CrMo4-5 quenched and tempered (+QT)
- EN 10083-1 Grade 42CrMo4 surface hardened
Get a quote