ASTM A193 Grade B8 Class 1, Carbide solution treated
Equivalent material: DIN 1.4301, DIN X 5 CrNi 18 9, DIN X5CrNi18-10, AFNOR Z6CN18-09, AFNOR Z7CN18-09, BS 304S15, BS 304S31, UNI X5CrNi1810, SS 2332, UNE F.3551, AISI 304, SAE 304, JIS SUS304, JIS SUS304TBS, JIS SUS304TPD, JIS SUS304TP, JIS SUS304TPY, JIS SUS304TB, JIS SUS304TF, JIS SUS304TKA, JIS SUS304TKC, JIS SUSF304, EN X5CrNi18-10, EN 1.4301, ISO A2, GOST 08Ch18N10, GB 0Cr18Ni9, ASTM TP304, ASTM Grade B8, ASTM Grade B8A, UNS S30400
ASTM A193 Grade B8 Class 1, Carbide solution treated general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
ASTM A193 Grade B8 Class 1, Carbide solution treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1375 - 1450 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
ASTM A193 Grade B8 Class 1, Carbide solution treated chemical
| Property |
Value |
| Carbon |
Carbon of 0.08 % |
| Chromium |
Chromium of 18 - 20 % |
| Manganese |
Manganese of 2 % |
| Nickel |
Nickel of 8 - 11 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
ASTM A193 Grade B8 Class 1, Carbide solution treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
ASTM A193 Grade B8 Class 1, Carbide solution treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A50 |
20.0 °C |
Elongation A50 of 30 % |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 223 [-] |
- |
| Hardness, Rockwell B |
20.0 °C |
Hardness, Rockwell B of 96 [-] |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Reduction of area |
20.0 °C |
Reduction of area of 50 % |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 515 MPa |
- |
| Yield Strength Rp0.2, short transverse |
20.0 °C |
Yield Strength Rp0.2, short transverse of 205 MPa |
- |